Supreme Petrochem SH 2114 High Impact Polystyrene

Category	Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified
Manufacturer	Supreme Petrochem LTD
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Supreme Petrochem SH 2114 High Impact Polystyrene.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Characteristics Very high impact strength Easy processing High heat Processing Extrusion MoldingApplications Toys, shoe heels, cosmetic boxes, pill vials Luggage cases Blending with clear polystyrene for translucent cups and lidsMaterial Status: Commercial : ActiveAgency Ratings: FDA 21 CFR 177.1640Information provided by Supreme Petrochem LTD

Physical Properties	Metric	English	Comments
Specific Gravity	1.03 g/cc	1.03 g/cc	ASTM D792
Melt Flow	2.2 g/10 min @Load 5.00 kg, Temperature 200 Â°C	2.2 g/10 min @Load 11.0 lb, Temperature 392 Â°F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	29.4 MPa	4260 psi	50 mm/min; ASTM D638
Elongation at Break	50 %	50 %	50 mm/min; ASTM D638
Flexural Strength	49.0 MPa @Thickness 3.20 mm	7110 psi @Thickness 0.126 in	ASTM D790
Flexural Modulus	1.81 GPa @Thickness 3.20 mm	263 ksi @Thickness 0.126 in	ASTM D790
Izod Impact, Notched	1.20 J/cm @Thickness 3.20 mm	2.25 ft-lb/in @Thickness 0.126 in	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	83.0 Â°C	181 Â°F	ASTM D648
Vicat Softening Point	105 Â°C	221 Â°F	1kg / 120Â°C; ASTM D1525
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in

Processing Properties	Metric	English	Comments
Melt Temperature	180 - 260 Â°C	356 - 500 Â°F
Mold Temperature	40.0 - 60.0 Â°C	104 - 140 Â°F