Sumitomo Bakelite North America FS-10-VO-200-P Short-Glass Reinforced Diallyl Phthalate

Category Polymer , Thermoset , Diallyl Phthalate (DAP) , Diallyl Phthalate (DAP) Molding Compound, Short Glass Fiber Filled , Filled/Reinforced Thermoset
Manufacturer Sumitomo Bakelite North America
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Sumitomo Bakelite North America FS-10-VO-200-P Short-Glass Reinforced Diallyl Phthalate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Short glass fiber reinforced, flame retardant, diallyl meta-phthalate molding compound with excellent heat resistance.Meets the requirements of ASTM D5948 Type SIG-F.Information provided by Vyncolit, a Sumitomo Bak Group
Physical Properties Metric English Comments
Density 1.91 g/cc
0.0690 lb/in³
Relative Density; ASTM D792
Linear Mold Shrinkage 0.0020 - 0.0040 cm/cm
0.0020 - 0.0040 in/in
Compression Molding; ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 75.8 MPa
11000 psi
ASTM D638
Flexural Strength 131 MPa
19000 psi
At Rupture; ASTM D790
Flexural Modulus 11.7 GPa
1700 ksi
ASTM D790
Compressive Strength 152 MPa
22000 psi
ASTM D695
Izod Impact, Notched 0.320 J/cm
0.599 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 18.0 µm/m-°C

@Temperature 20.0 °C
10.0 µin/in-°F

@Temperature 68.0 °F
ASTM E-831
Thermal Conductivity 0.360 W/m-K
2.50 BTU-in/hr-ft²-°F
ASTM C-518
Maximum Service Temperature, Air 200 °C
392 °F
UL 746B
Deflection Temperature at 1.8 MPa (264 psi) >= 260 °C
>= 500 °F
As molded; ASTM D648
Flammability, UL94 V-0

@Thickness 1.60 mm
V-0

@Thickness 0.0630 in
V-0

@Thickness 3.20 mm
V-0

@Thickness 0.126 in
Oxygen Index 50 %
50 %
ASTM D2863
Electrical Properties Metric English Comments
Dielectric Constant 3.9

@Frequency 1e+6 Hz
3.9

@Frequency 1e+6 Hz
Wet; ASTM D150
4.1

@Frequency 1000 Hz
4.1

@Frequency 1000 Hz
wet; ASTM D150
Dielectric Strength 14.8 kV/mm
376 kV/in
60Hz, Step-by-Step, wet; ASTM D149
Dissipation Factor 0.011

@Frequency 1000 Hz
0.011

@Frequency 1000 Hz
wet; ASTM D150
0.016

@Frequency 1e+6 Hz
0.016

@Frequency 1e+6 Hz
wet; ASTM D150
Arc Resistance 175 sec
175 sec
ASTM D495
Comparative Tracking Index >= 600 V
>= 600 V
IEC 112
Descriptive Properties Value Comments
Color Blue, Dark Gray
Flammability: Burning, sec 50
ASTM D229
Flammability: Ignition, sec 130
ASTM D229
Form Granular
Main Filler Glass Fiber
Molding Method Compression, transfer, injection