Sumitomo Bakelite North America FM 3001 Cellulose Reinforced Phenolic Novolac

Category	Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic , Phenolic, Novolac, Cellulose Filled
Manufacturer	Sumitomo Bakelite North America
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Sumitomo Bakelite North America FM 3001 Cellulose Reinforced Phenolic Novolac.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

FM 3001 is a self-lubricated cellulose reinforced phenolic molding compound, modified for applications requiring reduced friction and low wear. Information supplied by Sumitomo Bak North America.

Physical Properties	Metric	English	Comments
Bulk Density	0.450 g/cc	0.0163 lb/inÂ³	Powder; ASTM D1895
Density	1.41 g/cc	0.0509 lb/inÂ³	ASTM D-792
Water Absorption	0.60 %	0.60 %	24 hour; ASTM D570
	1.2 %	1.2 %	48 hour; ASTM D570
Linear Mold Shrinkage	0.0030 cm/cm	0.0030 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell E	115	115	ASTM D785
Tensile Strength, Ultimate	42.0 MPa	6090 psi	ASTM D638
Flexural Strength	60.0 MPa	8700 psi	ASTM D790
Flexural Modulus	7.60 GPa	1100 ksi	ASTM D790
Compressive Strength	160 MPa	23200 psi	ASTM D695
Izod Impact, Notched	0.320 J/cm	0.599 ft-lb/in	ASTM D256A

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	24.0 Âµm/m-Â°C @Temperature 20.0 Â°C	13.3 Âµin/in-Â°F @Temperature 68.0 Â°F	ASTM E831
Deflection Temperature at 1.8 MPa (264 psi)	180 Â°C	356 Â°F	As Molded; ASTM D648A

Descriptive Properties	Value	Comments
Available Molding Grades	Compression, Transfer, Injection
Color	Black
Form	Granular