- Sumitomo Bakelite North America 52-40-40-P Long-Glass Reinforced Diallyl Phthalate
Sumitomo Bakelite North America 52-40-40-P Long-Glass Reinforced Diallyl Phthalate
| Category | Polymer , Thermoset , Diallyl Phthalate (DAP) , Diallyl Phthalate (DAP) Molding Compound, Short Glass Fiber Filled , Filled/Reinforced Thermoset |
| Manufacturer | Sumitomo Bakelite North America |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sumitomo Bakelite North America 52-40-40-P Long-Glass Reinforced Diallyl Phthalate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ortho Resin Isomer (DAP). Used for critical, high-performance military and commercial electrical components where long-term reliability is demanded.Meets the requirements of ASTM D5948 Type GDI-30F.Information provided by Sumitomo Bak North America, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.79 g/cc | 0.0647 lb/in³ | ASTM D792 |
| Apparent Bulk Density | 0.300 g/cc | 0.0108 lb/in³ | |
| Water Absorption | 0.32 % | 0.32 % | 48 hours, 50°C. ASTM D570 |
| Linear Mold Shrinkage | 0.0015 - 0.0035 cm/cm | 0.0015 - 0.0035 in/in | Compression Molding. ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Yield Strength | 125 MPa | 18100 psi | ASTM D790 |
| Flexural Modulus | 13.8 GPa | 2000 ksi | ASTM D790 |
| Compressive Yield Strength | 187 MPa | 27100 psi | ASTM D695 |
| Izod Impact, Notched | 0.52 J/cm | 0.97 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 22.0 µm/m-°C @Temperature 20.0 °C |
12.2 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Thermal Conductivity | 0.314 W/m-K | 2.18 BTU-in/hr-ft²-°F | ASTM F433 |
| Deflection Temperature at 1.8 MPa (264 psi) | 260 °C | 500 °F | as molded; ASTM D648 |
| >= 280 °C | >= 536 °F | post baked; ASTM D648 | |
| Oxygen Index | 30 % | 30 % | ASTM D2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 4.3 @Frequency 1e+6 Hz |
4.3 @Frequency 1e+6 Hz |
Wet |
| 4.4 @Frequency 1000 Hz |
4.4 @Frequency 1000 Hz |
Wet | |
| Dielectric Strength | 16.9 kV/mm @Frequency 60.0 Hz |
429 kV/in @Frequency 60.0 Hz |
Wet, step by step; ASTM D149 |
| Dissipation Factor | 0.010 @Frequency 1000 Hz |
0.010 @Frequency 1000 Hz |
Wet; ASTM D150 |
| 0.016 @Frequency 1e+6 Hz |
0.016 @Frequency 1e+6 Hz |
Wet; ASTM D150 | |
| Arc Resistance | 133 sec | 133 sec | ASTM D495 |
| Comparative Tracking Index | >= 600 V | >= 600 V | ASTM D3638 (IEC 112) |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 160 - 180 °C | 320 - 356 °F | Mold temperature |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Flammability, Burning, sec | 60 | ASTM D229 |
| Flammability, Ignition, sec | 90 | ASTM D229 |
Users viewing this material also viewed the following:
- Lotte Chemical Titan TITANLENE® LDF201FG Low density polyethylene
- Tisan TISLAMID® 66 15% Mineral Filled Flame Retardant (V0). Heat Stabilized Nylon 66
- A. Schulman POLYFORT™ FPP 3715 Glass Filled Homopolymer Polypropylene
- Covestro Makrolon® 2405 MAS056 Polycarbonate
- Crucible Steel CPM® Rex® 20® (HS) High Speed Steel
- Daikin DAI-EL G-902 Fluoroelastomer Terpolymer, Peroxide Curable Grade, 71% Fluorine Content
- 3M 12026 Black 1/16" (1.6 mm) Polyurethane Foam
- BASF 2-Ethylhexyl Choroformate
- BCC Products BC 100 Thick Cyanoacrylate Adhesive
- DuPont Performance Polymers Sorona® 3301V BK001 Polytrimethylene Terephthalate (PTT) (Unverified Data**)&
Copyright © lookpolymers.com All Rights Reserved