- Styron Pulse® B-270 PC/ABS
Styron Pulse® B-270 PC/ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Styron |
| Trade Name | Pulse® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styron Pulse® B-270 PC/ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Engineering ResinInformation provided by DowThis product line was spun off from Dow Chemical to Styron in 2010.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.21 g/cc | 1.21 g/cc | ASTM D792 |
| Water Absorption | 0.050 % | 0.050 % | 23°C, 24hrs; ASTM D570 |
| Water Absorption at Saturation | 0.18 % | 0.18 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0065 cm/cm | 0.0065 in/in | ASTM D955 |
| Melt Flow | 1.5 g/10 min @Load 3.80 kg, Temperature 230 °C |
1.5 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 51.4 MPa | 7450 psi | ASTM D638 |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | ASTM D638 |
| Elongation at Break | 100 % | 100 % | ASTM D638 |
| Flexural Yield Strength | 100 MPa | 14500 psi | ASTM D790 |
| Flexural Modulus | 3.30 GPa | 479 ksi | ASTM D790 |
| Izod Impact, Notched | 1.10 J/cm @Thickness 3.20 mm, Temperature -29.0 °C |
2.06 ft-lb/in @Thickness 0.126 in, Temperature -20.2 °F |
ASTM D256 |
| 3.70 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
6.93 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 | |
| Dart Drop, Total Energy | 56.5 J @Thickness 3.20 mm, Temperature -29.0 °C |
41.7 ft-lb @Thickness 0.126 in, Temperature -20.2 °F |
ASTM D3763 |
| 56.5 J @Thickness 3.20 mm, Temperature 23.0 °C |
41.7 ft-lb @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 134 °C @Thickness 81.3 mm |
273 °F @Thickness 3.20 in |
ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 277 - 294 °C | 531 - 561 °F | |
| Mold Temperature | 71.0 - 94.0 °C | 160 - 201 °F | |
| Drying Temperature | 98.9 °C | 210 °F | |
| Dry Time | 4 hour | 4 hour |
Users viewing this material also viewed the following:
- RheTech Products P254-00 Polypropylene Copolymer, Natural
- NanoAmor 95%; OD: 200-500 nm Graphitized Carbon Nanofibers
- Polykemi AB POLYfill PPC 12000 Polypropylene Copolymer
- Master Bond EP30-2 Low Outgassing, Low Viscosity Two Component Epoxy
- Dow Buna® SB 1721 Cold polymerized Emulsion Styrene Butadiene Rubber (E-SBR)
- ELM® Biobased Dust Suppressant & Stabilizer
- BASF Basantol® 415 Bordeaux Liquid
- BASF N-Ethylpiperidine
- Arkema Group Rilsan® AESN P40 TL Nylon 12, Flexible Tubing Grade (Conditioned)
- AK Steel 316 Austenitic Stainless steel
Copyright © lookpolymers.com All Rights Reserved