Styron Pulse® A35-110 PC/ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Styron |
| Trade Name | Pulse® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styron Pulse® A35-110 PC/ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PULSEâ„¢ A35-110 engineering resins give exceptional impact strength even at low temperatures and have high heat distortion temperature. The proprietary mass ABS technology of Dow allows these physical properties to be achieved together with superior flow performance, for easy molding of complex parts and design freedom.Information provided by DowThis product line was spun off from Dow Chemical to Styron in 2010.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ISO R1183 B |
| Water Absorption | 0.20 - 0.60 % | 0.20 - 0.60 % | ISO R 62 |
| Linear Mold Shrinkage | 0.0030 - 0.0070 cm/cm | 0.0030 - 0.0070 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 105 MPa | 15200 psi | DIN 53459 |
| Tensile Strength at Break | 53.0 MPa | 7690 psi | 5 mm/min; ISO R 527 |
| Tensile Strength, Yield | 58.0 MPa | 8410 psi | 5 mm/min; ISO R 527 |
| Elongation at Break | >= 80 % | >= 80 % | 5 mm/min; ISO R 527 |
| Elongation at Yield | 5.0 % | 5.0 % | 5 mm/min; ISO R 527 |
| Tensile Modulus | 2.35 GPa | 341 ksi | 1 mm/min; ISO R 527 |
| Flexural Strength | 85.0 MPa | 12300 psi | 1 mm/min; ISO 178 |
| Flexural Modulus | 2.20 GPa | 319 ksi | 3 points and 1 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 50.0 kJ/m² @Temperature -40.0 °C |
23.8 ft-lb/in² @Temperature -40.0 °F |
ISO R 180 |
| 70.0 kJ/m² @Temperature 23.0 °C |
33.3 ft-lb/in² @Temperature 73.4 °F |
ISO R 180 | |
| Charpy Impact Unnotched | NB @Temperature -40.0 °C |
NB @Temperature -40.0 °F |
ISO R 179 |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO R 179 | |
| Charpy Impact, Notched | 1.50 J/cm² @Temperature -40.0 °C |
7.14 ft-lb/in² @Temperature -40.0 °F |
ISO R179 |
| 2.60 J/cm² @Temperature 0.000 °C |
12.4 ft-lb/in² @Temperature 32.0 °F |
ISO R179 | |
| 3.50 J/cm² @Temperature 23.0 °C |
16.7 ft-lb/in² @Temperature 73.4 °F |
ISO R179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 75.0 - 80.0 µm/m-°C @Temperature 0.000 - 80.0 °C |
41.7 - 44.4 µin/in-°F @Temperature 32.0 - 176 °F |
ASTM D696 |
| Thermal Conductivity | 0.200 W/m-K | 1.39 BTU-in/hr-ft²-°F | ASTM C177 |
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C | 266 °F | unannealed; ISO 75 B |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | unannealed; ISO 75 A |
| Vicat Softening Point | 132 °C | 270 °F | 50°C/hr, 5 kg; ISO 306 B |
| 145 °C | 293 °F | 120°C/hr, 1 kg; ISO 306 A | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| Oxygen Index | 21 % | 21 % | ASTM D2863 |
Users viewing this material also viewed the following:
- Quadrant EPP Acetron® MD Metal-detectable Copolymer Acetal (ASTM Product Data Sheet)
- Solvay Specialty Polymers Mindel® B-430 Polysulfone, Modified (PSU, Modified) (discontinued **)
- Inno-Comp INNOPOL® CS 1-2140 BLH 40% Talc-Filled Polypropylene Homopolymer
- Haynes 25 alloy, room temperature sheet after 100 hours of 760°C exposure
- Solvay Specialty Polymers Udel® P-3500 LCD Polysulfone (PSU)
- Spartech SP-2010 HIPS Polystyrene Sheet
- Sibur 21030-PM1 Polypropylene with Low Haze
- Wanhua Chemical Wanthane® WHT-1565 Polyester Based TPU
- Diamond Polymers ABS 7501 E
- Ineos Nova 5540 High Impact Polystyrene (discontinued **)