- Styron Pulse® 959 ABS + Polycarbonate, 10% Glass Reinforced
Styron Pulse® 959 ABS + Polycarbonate, 10% Glass Reinforced
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Glass Fiber Filled , Polycarbonate (PC) |
| Manufacturer | Styron |
| Trade Name | Pulse® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styron Pulse® 959 ABS + Polycarbonate, 10% Glass Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PULSE® 959 Engineering resin is a 10% glass reinforced resin designed to provide excellent processability, high heat resistance, and practical toughness. PULSE 959 Engineering resin has been used in automotive interior trim applications.Data provided by Dow Chemical.This product line was spun off from Dow Chemical to Styron in 2010.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | ASTM Data |
| Melt Density | 1.05 g/cc | 0.0379 lb/in³ | Melt density |
| Water Absorption | 0.15 % | 0.15 % | |
| Moisture Absorption at Equilibrium | 0.32 % | 0.32 % | Humidity Absorption |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | |
| Melt Flow | 1.5 g/10 min @Load 3.80 kg, Temperature 230 °C |
1.5 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM Data |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | |
| Tensile Strength, Ultimate | 50.4 MPa | 7310 psi | ASTM Data |
| Tensile Strength, Yield | 48.8 MPa | 7080 psi | ASTM Data |
| Elongation at Break | 4.0 % | 4.0 % | ASTM Data |
| Elongation at Yield | 3.4 % | 3.4 % | ISO Data |
| Tensile Modulus | 3.80 GPa | 551 ksi | ISO Data. |
| Izod Impact, Notched | 1.60 J/cm | 3.00 ft-lb/in | ASTM Data |
| 0.801 J/cm @Temperature -50.0 °C |
1.50 ft-lb/in @Temperature -58.0 °F |
ASTM Data | |
| Charpy Impact Unnotched | 5.00 J/cm² | 23.8 ft-lb/in² | ISO Data, Low Temp |
| 9.00 J/cm² | 42.8 ft-lb/in² | ISO Data | |
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | ISO Data, Low Temp |
| 1.80 J/cm² | 8.57 ft-lb/in² | ISO Data | |
| Impact Test | 5.65 J @Temperature -30.0 °C |
4.17 ft-lb @Temperature -22.0 °F |
Instrumented Dart Total Energy |
| 12.4 J @Temperature 23.0 °C |
9.15 ft-lb @Temperature 73.4 °F |
Instrumented Dart Total Energy |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 57.6 µm/m-°C @Temperature 20.0 °C |
32.0 µin/in-°F @Temperature 68.0 °F |
ASTM data |
| Specific Heat Capacity | 2.15 J/g-°C | 0.514 BTU/lb-°F | |
| Thermal Conductivity | 0.228 W/m-K | 1.58 BTU-in/hr-ft²-°F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 121 °C | 250 °F | Unannealed; 127°C (261°F) annealed; ASTM Data |
Users viewing this material also viewed the following:
- Indium Corp. 99.9% InI3 Indium Triiodide
- Kolon KOPEL® KP3855FB Polyester Elastomer Resin (TPE)
- Lubrizol Advanced Materials PEARLBOND® 522 Linear Thermoplastic Polyurethane
- H.C. Starck Amperit® 518.001 Agglomerated, Sintered Tungsten Carbide-Cobalt 88-12 (WC-CO)
- Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes
- SABIC Innovative Plastics LNP THERMOCOMP DX06094 PC (Europe-Africa-Middle East)
- Solvay Chemicals Ammonium Hydrogen Fluoride
- Polyram PlusTek PA303G43 Nylon 6.6, 43% Glass Fiber
Copyright © lookpolymers.com All Rights Reserved