Styron Pulse® 920 MG PC/ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate (PC) |
| Manufacturer | Styron |
| Trade Name | Pulse® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styron Pulse® 920 MG PC/ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
An inherently matt medium heat, medium impact PC/ABS resin, PULSEâ„¢ 920 MG is designed for interior automotive applications where a matt aesthetic is required.Information provided by DowThis product line was spun off from Dow Chemical to Styron in 2010.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 3.5 g/10 min @Load 3.80 kg, Temperature 230 °C |
3.5 g/10 min @Load 8.38 lb, Temperature 446 °F |
ISO 1133 |
| 17 g/10 min @Load 5.00 kg, Temperature 260 °C |
17 g/10 min @Load 11.0 lb, Temperature 500 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 44.0 MPa | 6380 psi | ISO 527 |
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | 100mm/min; ISO 527 |
| Elongation at Break | 100 % | 100 % | 100mm/min; ISO 527 |
| Tensile Modulus | 2.25 GPa | 326 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 85.0 MPa | 12300 psi | 2mm/min; ISO 178 |
| Flexural Modulus | 2.10 GPa | 305 ksi | 3 points and 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 20.0 kJ/m² @Temperature -30.0 °C |
9.52 ft-lb/in² @Temperature -22.0 °F |
ISO 180 |
| 45.0 kJ/m² @Temperature 23.0 °C |
21.4 ft-lb/in² @Temperature 73.4 °F |
ISO 180 | |
| Charpy Impact, Notched | 0.700 J/cm² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| 2.20 J/cm² @Temperature 23.0 °C |
10.5 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 75.0 - 80.0 µm/m-°C @Temperature 0.000 - 80.0 °C |
41.7 - 44.4 µin/in-°F @Temperature 32.0 - 176 °F |
ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | unannealed; ISO 75-A |
| Vicat Softening Point | 122 °C | 252 °F | 50N / 50°C (unannealed); ISO 306B |
| 142 °C | 288 °F | 10N / 120°C (unannealed); ISO 306A | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 250 - 290 °C | 482 - 554 °F | |
| Mold Temperature | 50.0 - 90.0 °C | 122 - 194 °F |
Users viewing this material also viewed the following:
- Ineos HP54-60 Flake Polyethylene Copolymer Flake
- Momentive Performance Materials PolarTherm® PT110 Boron Nitride (BN) Powder
- SABIC Innovative Plastics Valox® SHF4930 PBT
- SABIC Innovative Plastics LNP VERTON UF-700-12 HS EXP PPA (Asia Pacific)
- Dow Corning SYL-OFF® SL 7688 RELEASE COATING
- DSM Akulon® K224-LGM35 (Dry) 15% Glass Reinforced, 25% Mineral Reinforced Nylon 6 (North America)
- Eurotec® Tecomid® NA40 AR20 NL HS PA6.6, 20% aramid fiber reinforced, heat stabilized, natural
- 3M Scotchcal™ ElectroCut™ 7725-49 Graphic Film
- Momentive Performance Materials PolarTherm® PT350 Boron Nitride (BN) Powder
- Haynes Hastelloy® C-22® alloy, transverse, SMAW weldment, 19.1 mm thick plate
Copyright © lookpolymers.com All Rights Reserved