Styron PULSEâ„¢ 2000 EZ PC/ABS Engineering Resin

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer Styron
Trade Name PULSE™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Styron PULSEâ„¢ 2000 EZ PC/ABS Engineering Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Overview: PULSE 2000 Engineering Resin is designed to provide top performance in tough applications, from single piece items to intricate components. Ideal for energy management solutions, it can withstand high and low temperature extremes and rapid, repeated temperature fluctuations.Benefits:Instrument panelsKnee bolstersRetainersInterior trimInformation provided by Styron
Physical Properties Metric English Comments
Density 1.13 g/cc
0.0408 lb/in³
ASTM D792; ISO 1183/B
Water Absorption 0.15 %

@Temperature 23.0 °C,
Time 86400 sec
 0.15 %

@Temperature 73.4 °F,
Time 24.0 hour
 ASTM D570; ISO 62
Linear Mold Shrinkage 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
ISO 294-4
Melt Flow 18 g/10 min
18 g/10 min
ASTM D1238
18 g/10 min

@Load 5.00 kg,
Temperature 260 °C
 18 g/10 min

@Load 11.0 lb,
Temperature 500 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 55.0 MPa
7980 psi
50 mm/min; ASTM D638
47.0 MPa

@Thickness 4.00 mm
 6820 psi

@Thickness 0.157 in
 Injection Molded; ISO 527-2/50
Tensile Strength, Yield 58.0 MPa
8410 psi
50 mm/min; ASTM D638
57.0 MPa

@Thickness 4.00 mm
 8270 psi

@Thickness 0.157 in
 Injection Molded; ISO 527-2/50
Elongation at Break 160 %
160 %
ASTM D638
90 %

@Thickness 4.00 mm
 90 %

@Thickness 0.157 in
 Injection Molded; ISO 527-2/50
Elongation at Yield 4.5 %

@Thickness 4.00 mm
 4.5 %

@Thickness 0.157 in
 Injection Molded; ISO 527-2/50
Tensile Modulus 2.33 GPa

@Thickness 4.00 mm
 338 ksi

@Thickness 0.157 in
 Injection Molded; ISO 527-2
Flexural Strength 90.0 MPa

@Thickness 4.00 mm
 13100 psi

@Thickness 0.157 in
 Injection Molded, 2 mm/min; ISO 178
Flexural Modulus 2.45 GPa
355 ksi
1.3 mm/min.; ASTM D790
2.40 GPa

@Thickness 4.00 mm
 348 ksi

@Thickness 0.157 in
 Injection Molded, 2 mm/min; ISO 178
Izod Impact, Notched (ISO) 0.590 kJ/m²

@Temperature -30.0 °C
 0.281 ft-lb/in²

@Temperature -22.0 °F
 ASTM D256
0.750 kJ/m²

@Temperature 23.0 °C
 0.357 ft-lb/in²

@Temperature 73.4 °F
 ASTM D256
47.0 kJ/m²

@Temperature -30.0 °C
 22.4 ft-lb/in²

@Temperature -22.0 °F
 ISO 180/A
63.0 kJ/m²

@Temperature 23.0 °C
 30.0 ft-lb/in²

@Temperature 73.4 °F
 ISO 180/A
Dart Drop, Total Energy 62.0 J
45.7 ft-lb
2.2 m/sec; ASTM D3763
55.0 J

@Temperature 23.0 °C
 40.6 ft-lb

@Temperature 73.4 °F
 2.2 m/sec; ASTM D3763
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 109 °C
228 °F
Unannealed; ASTM D648
130 °C
266 °F
Unannealed; ISO 75-2/B
Deflection Temperature at 1.8 MPa (264 psi) 106 °C
223 °F
Unannealed; ISO 75-2/A
Vicat Softening Point 129 °C
264 °F
ISO 306/B50
142 °C
288 °F
ISO 306/A120
Flame Spread <= 100 mm/min
<= 3.94 in/min
FMVSS 305