Styron Magnum™ 9020 ABS, High Gloss

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded
Manufacturer Styron
Trade Name Magnum™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Styron Magnum™ 9020 ABS, High Gloss.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
MAGNUM® ABS resins are thermoplastic materials which provide an excellent balance of processability, impact resistance and heat resistance as imparted by the various polymer compositions. MAGNUM ABS resin are available in a wide range of melt flow rates, impact strength and heat resistance for both high and low gloss applications manufactured by injection molding, sheet or profile extrusion and thermoforming.The MAGNUM 9000 series of high gloss ABS resins are designed to offer a wide range of impact strengths and melt flow rates to meet the needs of the durables injection molding markets. The 9000 series products offer typical Izod impact strength values from 210 to 400 J/m and melt flow rates ranging from 2.5 to 7.0 g/10min. The gloss values are typically greater than 95% on the 60. Gardner scale for the highest gloss resins and greater than 90% for those products having a broader range of gloss.MAGNUM 9020 ABS resin is one of the highest gloss resin with a high impact strength and medium flow. MAGNUM 9020 is used primarily in injection molding durable applications like floor care and outdoor equipment where a good balance between impact strength and processability is needed.Data provided by Dow Chemical.This product line was spun off from Dow Chemical to Styron in 2010.
Physical Properties Metric English Comments
Density 1.04 g/cc
0.0376 lb/in³
ASTM Data
Melt Density 0.975 g/cc
0.0352 lb/in³
Melt density
Linear Mold Shrinkage 0.0055 cm/cm
0.0055 in/in
Melt Flow 5.0 g/10 min

@Load 3.80 kg,
Temperature 230 °C
5.0 g/10 min

@Load 8.38 lb,
Temperature 446 °F
ASTM Data
Mechanical Properties Metric English Comments
Hardness, Rockwell R 107
107
Tensile Strength, Ultimate 33.1 MPa
4800 psi
ASTM Data
Tensile Strength, Yield 41.4 MPa
6000 psi
ASTM Data
Elongation at Break 50 %
50 %
ASTM Data
Elongation at Yield 2.5 %
2.5 %
ISO Data
Tensile Modulus 2.07 GPa
300 ksi
ASTM Data
Izod Impact, Notched 2.94 J/cm
5.51 ft-lb/in
ASTM Data
Charpy Impact Unnotched 8.00 J/cm²
38.1 ft-lb/in²
ISO Data, Low Temp
NB
NB
ISO Data
Charpy Impact, Notched 0.800 J/cm²
3.81 ft-lb/in²
ISO Data, Low Temp
2.40 J/cm²
11.4 ft-lb/in²
ISO Data
Impact Test 50.0 J

@Temperature 23.0 °C
36.9 ft-lb

@Temperature 73.4 °F
Instrumented Dart Total Energy
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 102 µm/m-°C

@Temperature 20.0 °C
56.7 µin/in-°F

@Temperature 68.0 °F
ISO data
Specific Heat Capacity 2.13 J/g-°C
0.509 BTU/lb-°F
Thermal Conductivity 0.187 W/m-K
1.30 BTU-in/hr-ft²-°F
Deflection Temperature at 0.46 MPa (66 psi) 94.0 °C
201 °F
Unannealed; ASTM Data
Deflection Temperature at 1.8 MPa (264 psi) 79.0 °C
174 °F
Unannealed; 104°C (219°F) annealed; ASTM Data
Vicat Softening Point 108 °C
226 °F
Flammability, UL94 HB

@Thickness 1.47 mm
HB

@Thickness 0.0579 in
Optical Properties Metric English Comments
Gloss 95 %
95 %
Gardner Gloss, 60°