Styron Magnumâ„¢ 8391 MED Acrylonitrile Butadiene Styrene (ABS) Resin

Category Polymer , Thermoplastic , ABS Polymer
Manufacturer Styron
Trade Name Magnum™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Styron Magnumâ„¢ 8391 MED Acrylonitrile Butadiene Styrene (ABS) Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Overview: MAGNUMâ„¢ MED ABS combines an excellent glossy appearance with high flow and medium impact performance. The mass (continuous process) ABS technology of Styron ensures an ABS resin that combines excellent processablilty with a stable light base color that is ideal for self-coloring. MAGNUM 8391 MED natural resin has undergone biocompatibility testing based on ISO 10993 (Biological Evaluation of Medical Devices) and is suitable for use in approved medical applications. Applications:Medical ApplicationsInformation provided by Styron
Physical Properties Metric English Comments
Density 1.05 g/cc
0.0379 lb/in³
ASTM D792; ISO 1183/B
Apparent Bulk Density 0.650 g/cc
0.0235 lb/in³
ISO 60
Linear Mold Shrinkage, Flow 0.0040 - 0.0070 cm/cm
0.0040 - 0.0070 in/in
ASTM D955; ISO 294-4
Melt Flow 8.0 g/10 min

@Load 3.80 kg,
Temperature 230 °C
8.0 g/10 min

@Load 8.38 lb,
Temperature 446 °F
ASTM D1238
28 g/10 min

@Load 10.0 kg,
Temperature 220 °C
28 g/10 min

@Load 22.0 lb,
Temperature 428 °F
ASTM D1238; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 108
108
ASTM D785
Tensile Strength at Break 35.0 MPa
5080 psi
50 mm/min; ASTM D638
Tensile Strength, Yield 48.0 MPa
6960 psi
50 mm/min; ASTM D638
45.0 MPa

@Thickness 3.20 mm
6530 psi

@Thickness 0.126 in
Injection Molded; ISO 527-2/50
47.0 MPa

@Thickness 3.20 mm
6820 psi

@Thickness 0.126 in
Injection Molded; ISO 527-2/100
Elongation at Break 8.7 %
8.7 %
50 mm/min; ASTM D638
Elongation at Yield 2.7 %
2.7 %
50 mm/min; ASTM D638
2.5 %

@Thickness 3.20 mm
2.5 %

@Thickness 0.126 in
Injection Molded; ISO 527-2/50
2.6 %

@Thickness 3.20 mm
2.6 %

@Thickness 0.126 in
Injection Molded; ISO 527-2/100
Tensile Modulus 2.34 GPa
339 ksi
ISO 527-2
Flexural Strength 75.0 MPa
10900 psi
1.3 mm/min; ASTM D790
70.0 MPa

@Thickness 3.20 mm
10200 psi

@Thickness 0.126 in
3-point, 2 mm/min, Injection Molded; ISO 178
Flexural Modulus 2.48 GPa
360 ksi
1.3 mm/min; ASTM D790
2.40 GPa

@Thickness 3.20 mm
348 ksi

@Thickness 0.126 in
3-point, 2 mm/min, Injection Molded; ISO 178
Izod Impact, Notched 2.30 J/cm

@Temperature 23.0 °C
4.31 ft-lb/in

@Temperature 73.4 °F
Injection Molded; ASTM D256
Izod Impact, Notched (ISO) 9.00 kJ/m²

@Temperature -30.0 °C
4.28 ft-lb/in²

@Temperature -22.0 °F
Injection Molded; ISO 180/A
19.0 kJ/m²

@Temperature 23.0 °C
9.04 ft-lb/in²

@Temperature 73.4 °F
Injection Molded; ISO 180/A
Charpy Impact, Notched 0.900 J/cm²

@Temperature -30.0 °C
4.28 ft-lb/in²

@Temperature -22.0 °F
Injection Molded; ISO 179/1eA
1.90 J/cm²

@Temperature 23.0 °C
9.04 ft-lb/in²

@Temperature 73.4 °F
Injection Molded; ISO 179/1eA
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 87.0 °C
189 °F
Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 74.0 °C
165 °F
Unannealed; ASTM D648
95.0 °C
203 °F
Unannealed; ISO 75-2/A
Vicat Softening Point 95.0 °C
203 °F
ISO 306/B50
99.0 °C

@Load 1.02 kg
210 °F

@Load 2.25 lb
Rate B (120°C/h); ASTM D1525
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
Flame Spread 60.0 mm/min
2.36 in/min
ISO 3795