Styron Magnumâ„¢ 3453 Acrylonitrile Butadiene Styrene (ABS)
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | Styron |
| Trade Name | Magnum™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styron Magnumâ„¢ 3453 Acrylonitrile Butadiene Styrene (ABS).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
MAGNUMâ„¢ 3453 ABS is a general purpose injection molding resin suitable for a wide range of applications.Information provided by DowThis product line was spun off from Dow Chemical to Styron in 2010.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.650 g/cc | 0.0235 lb/in³ | ISO 60 |
| Density | 1.05 g/cc | 0.0379 lb/in³ | ISO 1183B |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ISO 294 |
| Melt Flow | 15 g/10 min @Load 10.0 kg, Temperature 220 °C |
15 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | 50mm/min; ISO 527-2 |
| Elongation at Yield | 2.5 % | 2.5 % | 50mm/min; ISO 527-2 |
| Tensile Modulus | 2.28 GPa | 331 ksi | ISO 527-2 |
| Flexural Strength | 68.0 MPa | 9860 psi | 3 points and 2 mm/min; ISO 178 |
| Flexural Modulus | 2.30 GPa | 334 ksi | 3 points and 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² @Temperature -30.0 °C |
4.28 ft-lb/in² @Temperature -22.0 °F |
ISO 180/A |
| 19.0 kJ/m² @Temperature 23.0 °C |
9.04 ft-lb/in² @Temperature 73.4 °F |
ISO 180/A | |
| Charpy Impact, Notched | 1.00 J/cm² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179-1/1eA |
| 2.00 J/cm² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | annealed; ISO 75-A |
| Vicat Softening Point | 97.0 °C | 207 °F | 50°C/hr, 50N; ISO 306-B50 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
|
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
||
| Flame Spread | 55 mm/min | 2.2 in/min | Horizontal Burning Speed 2mm thickness; ISO 3795 |
| Flammability Test | 25 | 25 | [µg/g] Carbon Emission; VDA 277 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 97 % | 97 % | ISO 294-4 |
Users viewing this material also viewed the following:
- JPJ Technologies LLDPE Virgin for Masterbatches
- Solvay MACKAZOLINE® O-V Surfactant
- Tisan TISOPLEN® 20% Talc Filled Heat Stabilized Copolymer Polypropylene
- Universal Wire Works 347 Stainless Steel (AMS 5680) Filler Metal
- Cossa Polimeri ESTALENE EN 25 C Modified Polyolefin Blend
- ELASTO UK Dryflex® 8006-101 Flame Retardant TPE for Extrusion, Natural, Halogen Free
- DSM Stanyl® TW200F6 (DAM) Nylon 46 30% Glass Reinforced, Heat Stabilized (North America)
- Arlon 19563R032 0.032" Cured Silicone Rubber with Fiberglass Substrate
- Arlon 51581R028 0.028" (0.711 mm) Uncured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved