Styron Magnumâ„¢ 3416 SC Natural Plus ABS Resin
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | Styron |
| Trade Name | Magnum™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styron Magnumâ„¢ 3416 SC Natural Plus ABS Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
The mass (continuous process) ABS technology of Dow ensures an ABS resin that combines excellent processability with sable light base color that is ideal for self-coloring.Information provided by DowThis product line was spun off from Dow Chemical to Styron in 2010.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.650 g/cc | 0.0235 lb/in³ | ISO 60 |
| Density | 1.05 g/cc | 0.0379 lb/in³ | ISO 1183B |
| Melt Flow | 2.2 g/10 min @Load 3.80 kg, Temperature 230 °C |
2.2 g/10 min @Load 8.38 lb, Temperature 446 °F |
ISO 1133 |
| 7.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
7.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 88 | 88 | ISO 2039/2 |
| Tensile Strength, Yield | 51.0 MPa | 7400 psi | 100mm/min; ISO DIS527/D |
| Elongation at Break | 25 % | 25 % | ISO DIS527/D |
| Tensile Modulus | 2.40 GPa | 348 ksi | 1mm/min; ISO DIS527/A |
| Flexural Strength | 76.0 MPa | 11000 psi | 1mm/min; ISO 178 |
| Flexural Modulus | 2.50 GPa | 363 ksi | 3 points; ISO 178 |
| 2.70 GPa | 392 ksi | 4 point; ISO 178 | |
| Shear Modulus | 0.960 GPa | 139 ksi | ISO 537 |
| Izod Impact, Notched (ISO) | 17.0 kJ/m² | 8.09 ft-lb/in² | ISO 180/1A |
| Charpy Impact Unnotched | NB | NB | ISO 179/2D |
| NB @Temperature -40.0 °C |
NB @Temperature -40.0 °F |
ISO 179/2D | |
| Charpy Impact, Notched | 0.700 J/cm² @Temperature -40.0 °C |
3.33 ft-lb/in² @Temperature -40.0 °F |
ISO 179/2C |
| 0.900 J/cm² @Temperature -20.0 °C |
4.28 ft-lb/in² @Temperature -4.00 °F |
ISO 179/2C | |
| 1.00 J/cm² @Temperature 0.000 °C |
4.76 ft-lb/in² @Temperature 32.0 °F |
ISO 179/2C | |
| 1.20 J/cm² @Temperature 23.0 °C |
5.71 ft-lb/in² @Temperature 73.4 °F |
ISO 179/2C |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 108 °C | 226 °F | annealed (120°C/hr); ISO 75-A |
| Vicat Softening Point | 108 °C | 226 °F | 50°C/hr, 5kg; ISO 306-B |
| 119 °C | 246 °F | 120°C/hr, 1kg; ISO 306-A | |
| Flammability, UL94 | HB | HB | all colors |
Users viewing this material also viewed the following:
- Raschig Group EPOXIDUR® 3582 EP Epoxy
- Saint-Gobain CHR® M99 Polyester Film Backing Acrylic Adhesive Pressure Sensitive Tape
- Styron CALIBREâ„¢ 200 10 Polycarbonate, General Purpose
- Dow Corning HV 495 Emulsion
- Ensinger Tecapeek® Classix Polyaryletherketone (PAEK)
- DuPont Performance Polymers Zytel® 70G30HSL NC010 Nylon 66 (Unverified Data**)
- Arlon Thermabond®-II 99760N008 0.008" (0.203 mm) Unsupported/Uncured Silicone Rubber with Fiberglass Substrate
- BASF Elastollan® 695A15N Polyester Type Polyurethane Elastomer
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 20 PHR Iceberg Clay Filler
- Solvay Specialty Polymers Algoflon® L101-1 Polytetrafluoroethylene (PTFE) (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved