- Styron Magnumâ„¢ 3325 MT Acrylonitrile Butadiene Styrene (ABS)
Styron Magnumâ„¢ 3325 MT Acrylonitrile Butadiene Styrene (ABS)
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | Styron |
| Trade Name | Magnum™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styron Magnumâ„¢ 3325 MT Acrylonitrile Butadiene Styrene (ABS).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
MAGNUMâ„¢ 3325 MT is resin with excellent processing characteristics and a matt surface finish. The mass (continuous process) ABS technology of Dow ensures an ABS resin that combines excellent processabiltiy with a stable light base color that is ideal for self coloring.Information provided by DowThis product line was spun off from Dow Chemical to Styron in 2010.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.650 g/cc | 0.0235 lb/in³ | ISO 60 |
| Density | 1.05 g/cc | 0.0379 lb/in³ | ISO 1183B |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ISO 294 |
| Melt Flow | 10 g/10 min @Load 10.0 kg, Temperature 220 °C |
10 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
| 11.55 g/10 min @Load 10.0 kg, Temperature 220 °C |
11.55 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 43.0 MPa | 6240 psi | 50mm/min; ISO 527-2 |
| Elongation at Yield | 3.3 % | 3.3 % | 50mm/min; ISO 527-2 |
| Tensile Modulus | 2.20 GPa | 319 ksi | ISO 527-2 |
| Flexural Strength | 65.0 MPa | 9430 psi | 3 points and 2 mm/min; ISO 178 |
| Flexural Modulus | 2.10 GPa | 305 ksi | 3 points and 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 180/A |
| 17.0 kJ/m² @Temperature 23.0 °C |
8.09 ft-lb/in² @Temperature 73.4 °F |
ISO 180/A | |
| Charpy Impact, Notched | 0.800 J/cm² @Temperature -30.0 °C |
3.81 ft-lb/in² @Temperature -22.0 °F |
ISO 179/2C (1984) |
| 1.10 J/cm² @Temperature -30.0 °C |
5.24 ft-lb/in² @Temperature -22.0 °F |
ISO 179-1/1eA | |
| 1.20 J/cm² @Temperature 23.0 °C |
5.71 ft-lb/in² @Temperature 73.4 °F |
ISO 179/2C (1984) | |
| 1.70 J/cm² @Temperature 23.0 °C |
8.09 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 101 °C | 214 °F | annealed; ISO 75-A |
| Vicat Softening Point | 102 °C | 216 °F | 50°C/hr, 50N; ISO 306-B50 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
|
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
||
| Flame Spread | 60 mm/min | 2.4 in/min | Horizontal Burning Speed 2mm thickness; ISO 3795 |
| Flammability Test | 20 | 20 | [mg/g] Carbon Emission; VDA 277 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 98 % | 98 % | ISO 6452 |