Styron Magnumâ„¢ 213 ABS, General Purpose

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded
Manufacturer Styron
Trade Name Magnum™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Styron Magnumâ„¢ 213 ABS, General Purpose.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
MAGNUM® ABS resins are thermoplastic materials which provide an excellent balance of processability, impact resistance and heat resistance as imparted by the various polymer compositions. MAGNUM ABS resin are available in a wide range of melt flow rates, impact strength and heat resistance for both high and low gloss applications manufactured by injection molding, sheet or profile extrusion and thermoforming.MAGNUM ABS resins offer a wide range of processability and impact resistance for low gloss injection molding applications. Combined with heat resistance and tensile and flexural strength, MAGNUM ABS resins are used in a wide variety of injection molding applications.MAGNUM 213 ABS resin is a low gloss, general purpose resin with easy flow. MAGNUM 213 has a melt flow rate of 5.5 g/10 min and a relatively low Izod impact strength of 105 J/m.Data provided by Dow Chemical.This product line was spun off from Dow Chemical to Styron in 2010.
Physical Properties Metric English Comments
Density 1.04 g/cc
0.0376 lb/in³
ASTM Data
Linear Mold Shrinkage 0.0055 cm/cm
0.0055 in/in
Melt Flow 5.5 g/10 min

@Load 3.80 kg,
Temperature 230 °C
5.5 g/10 min

@Load 8.38 lb,
Temperature 446 °F
ASTM Data
Mechanical Properties Metric English Comments
Hardness, Rockwell R 105
105
Tensile Strength, Ultimate 34.5 MPa
5000 psi
ASTM Data
Tensile Strength, Yield 29.6 MPa
4290 psi
ASTM Data
Elongation at Yield 1.7 %
1.7 %
ISO Data
Tensile Modulus 2.48 GPa
360 ksi
ASTM Data
Izod Impact, Notched 1.07 J/cm
2.00 ft-lb/in
ASTM Data
Charpy Impact Unnotched NB
NB
ISO Data
NB
NB
ISO Data, Low Temp
Charpy Impact, Notched 0.600 J/cm²
2.86 ft-lb/in²
ISO Data, Low Temp
0.900 J/cm²
4.28 ft-lb/in²
ISO Data
Impact Test 34.0 J

@Temperature 23.0 °C
25.1 ft-lb

@Temperature 73.4 °F
Instrumented Dart Total Energy
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 71.0 µm/m-°C

@Temperature 20.0 °C
39.4 µin/in-°F

@Temperature 68.0 °F
ISO data
Deflection Temperature at 1.8 MPa (264 psi) 73.9 °C
165 °F
Unannealed; ASTM Data
96.1 °C
205 °F
Annealed; ASTM Data
Vicat Softening Point 104 °C
219 °F
Flammability, UL94 HB

@Thickness 1.47 mm
HB

@Thickness 0.0579 in
Optical Properties Metric English Comments
Gloss 40 %
40 %
Gardner Gloss, 60°