Material Notes:
Overview: MAGNUM™ 342 EZ ABS resin is a medium impact, high flow, low gloss resin often used in automotive applications. Automotive MAGNUM ABS resins offer a wide range of gloss, viscosity, impact strength and heat properties for use in numerous automotive applications. Melt flow rates from 1 to 12 g/10 min, impact strengths from 2.5 to 12 ft-lb/in and heat distortion temperatures from 165 to 190°F are available. Available primarily as a natural plus concentrates, MAGNUM ABS resins are used in a wide variety of automotive applications including structural instrument panels, consoles, pillars, and exterior trim parts requiring painting and plating.Applications:Automotive door panelsConsolesInterior trimInformation provided by Styron
Physical Properties Metric English Comments
Density 1.04 g/cc
0.0376 lb/in³
ASTM D792
Maximum Moisture Content 0.10
0.10
Linear Mold Shrinkage, Flow 0.0040 - 0.0070 cm/cm
0.0040 - 0.0070 in/in
ASTM D955
Melt Flow 6.0 g/10 min

@Load 3.80 kg,
Temperature 230 °C
 6.0 g/10 min

@Load 8.38 lb,
Temperature 446 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 41.4 MPa

@Thickness 3.20 mm
 6000 psi

@Thickness 0.126 in
 Injection Molded; ASTM D638
Elongation at Yield 3.0 %

@Thickness 3.20 mm
 3.0 %

@Thickness 0.126 in
 Injection Molded; ASTM D638
Tensile Modulus 1.79 GPa

@Thickness 3.20 mm
 260 ksi

@Thickness 0.126 in
 1 mm/min, Injection Molded; ASTM D638
Flexural Strength 58.6 MPa

@Thickness 3.20 mm
 8500 psi

@Thickness 0.126 in
 Method I (3 point load), 2.0 mm/min, Injection Molded; ASTM D790
Flexural Modulus 2.00 GPa

@Thickness 3.20 mm
 290 ksi

@Thickness 0.126 in
 Method I (3 point load), 2.0 mm/min, Injection Molded; ASTM D790
Izod Impact, Notched 0.800 J/cm

@Thickness 3.20 mm,
Temperature -18.0 °C
 1.50 ft-lb/in

@Thickness 0.126 in,
Temperature -0.400 °F
 Injection Molded; ASTM D256
1.60 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
 3.00 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
 Injection Molded; ASTM D256
Dart Drop, Total Energy 32.8 J

@Thickness 3.20 mm,
Temperature 23.0 °C
 24.2 ft-lb

@Thickness 0.126 in,
Temperature 73.4 °F
 Injection Molded, Peak Energy; ASTM D3763
42.9 J

@Thickness 3.20 mm,
Temperature 23.0 °C
 31.6 ft-lb

@Thickness 0.126 in,
Temperature 73.4 °F
 Injection Molded, Total Energy; ASTM D3763
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 90.6 °C
195 °F
Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 76.7 °C
170 °F
Unannealed; ASTM D648
Vicat Softening Point 104 °C

@Load 1.02 kg
 219 °F

@Load 2.25 lb
 Rate B (120°C/h); ASTM D1525
Processing Properties Metric English Comments
Melt Temperature 232 - 246 °C
450 - 475 °F
Mold Temperature 26.7 - 48.9 °C
80.1 - 120 °F
Drying Temperature 82.2 - 85.0 °C
180 - 185 °F
Dry Time 2.00 - 4.00 hour
2.00 - 4.00 hour
Back Pressure 0.345 - 0.689 MPa
50.0 - 99.9 psi
Descriptive Properties Value Comments
Clamp Tonnage 2.8-4.1 kN/cm2
Screw Compression Ratio 1.5:1 to 3.5:1
Screw L/D Ratio 0.834027777777778