Styron EMERGEâ„¢ 5710 Acrylonitrile Butadiene Styrene (ABS)
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | Styron |
| Trade Name | EMERGE™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styron EMERGEâ„¢ 5710 Acrylonitrile Butadiene Styrene (ABS).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
EMERGEâ„¢ ABS 5710 advanced resin is an ignition resistant ABS resin with an excellent balance of flow and impact strength. Applications: Monitor Enclosures Surge Protectors and UPS Enclosures Information Technology Equipment Information provided by DowThis product line was spun off from Dow Chemical to Styron in 2010.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.18 g/cc | 1.18 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 11 g/10 min @Load 3.80 kg, Temperature 230 °C |
11 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 101 | 101 | ASTM D785 |
| Tensile Strength, Ultimate | 30.3 MPa | 4400 psi | 0.125 in, injection molded, unannealed; ASTM D638 |
| Tensile Strength, Yield | 36.5 MPa | 5300 psi | 0.125 in, injection molded, unannealed; ASTM D638 |
| Elongation at Break | 30.3 % | 30.3 % | 0.125 in, injection molded, unannealed; ASTM D638 |
| Elongation at Yield | 2.3 % | 2.3 % | 0.125 in, injection molded, unannealed; ASTM D638 |
| Flexural Strength | 63.4 MPa | 9200 psi | 0.125 in, injection molded, unannealed; ASTM D790 |
| Flexural Modulus | 2.49 GPa | 361 ksi | 0.125 in, injection molded, unannealed; ASTM D790 |
| Izod Impact, Notched | 2.03 J/cm | 3.80 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 70.2 µm/m-°C @Temperature -30.0 - 30.0 °C |
39.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 72.2 °C | 162 °F | unannealed (0.125 in); ASTM D648 |
| 76.1 °C | 169 °F | unannealed (0.250 in); ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 66.1 °C | 151 °F | unannealed (0.125 in); ASTM D648 |
| Vicat Softening Point | 83.9 °C | 183 °F | 120°C/hr, 10N; ASTM D1525 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
|
| V-0 @Thickness 2.00 mm |
V-0 @Thickness 0.0787 in |
||
| Oxygen Index | 28 % | 28 % | ASTM D2863 |
| Glow Wire Test | 950 °C @Thickness 2.00 mm |
1740 °F @Thickness 0.0787 in |
(GWFI); IEC 60695-2-12 |
| 950 °C @Thickness 2.00 mm |
1740 °F @Thickness 0.0787 in |
(GWIT); IEC 60695-2-13 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 180 - 210 °C | 356 - 410 °F | |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 3 - 4 hour | 3 - 4 hour |
Users viewing this material also viewed the following:
- Polystrand ThermoPro™ IE6010X X-Ply Cross-Ply Polypropylene-Glass Composite
- NOVA Chemicals EPS M77B Modified Expandable Polystyrene
- Custom Resins Norpex® SE1 PPE (Polyphenylene Ether) (discontinued **)
- EVALCA EVAL® K102 Ethylene Vinyl Alcohol Copolymer Resin (discontinued **)
- MetalTek MTEK D5 UNS T90405 Tool Steel
- Adell BJ-33 Nylon 6, 15% Glass Reinforced; High Impact
- 3M F-9465PC Adhesive Transfer Tape
- Overview of materials for Polycarbonate, Glass + PTFE Filled
- Aardvark Polymers Aarlon® 2000 Rotational Molding Resin, 50% RH
- Overview of materials for Polyether Block Amide (PEBA)
Copyright © lookpolymers.com All Rights Reserved