Styron CALIBREâ„¢ 7101 8 Polycarbonate, 10% Glass Reinforced

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Glass Fiber Filled, Flame Retardant
Manufacturer Styron
Trade Name CALIBRE™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Styron CALIBREâ„¢ 7101 8 Polycarbonate, 10% Glass Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
CALIBRE® 7101 is a 10% glass reinforced ignition resistant polycarbonate resin equipped with a mold release package for optimal processing. The CALIBRE 7101 resins exhibit a high modules, exceptional dimensional stability and are rated V-0 at 1.6 mm according to UL-94(1).CALIBRE 7101 polycarbonate resins are typically used for electrical boxes, lighting components and electrical switch connectors.Available Melt Flow Rates: 8, 10, 15.(1) These numerical flame spread ratings are small scale test values and are not intended to reflect hazards presented by these or any other materials under actual fire conditions.Ignition resistant chemical additives increase resistance to burning from minor flame sources and permit properly manufactured end products to meet the requirements of certain flammability tests, but resins will burn rapidly under the right conditions of heat and oxygen feed.Data provided by Dow Chemical.This product line was spun off from Dow Chemical to Styron in 2010.
Physical Properties Metric English Comments
Density 1.27 g/cc
0.0459 lb/in³
ASTM Data
Water Absorption 0.15 %
0.15 %
Moisture Absorption at Equilibrium 0.25 %
0.25 %
Humidity Absorption
Melt Flow 8.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
8.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM Data
Mechanical Properties Metric English Comments
Hardness, Rockwell R 122
122
Tensile Strength, Ultimate 63.0 MPa
9140 psi
ASTM Data
Tensile Strength, Yield 60.0 MPa
8700 psi
ASTM Data
Elongation at Break 4.0 %
4.0 %
ASTM Data
Elongation at Yield 4.0 %
4.0 %
ISO Data
Tensile Modulus 3.65 GPa
529 ksi
ASTM Data
Izod Impact, Unnotched 0.400 J/cm
0.749 ft-lb/in
ASTM Data
Impact Test 34.0 J

@Temperature 23.0 °C
25.1 ft-lb

@Temperature 73.4 °F
Instrumented Dart Total Energy
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 37.8 µm/m-°C

@Temperature 20.0 °C
21.0 µin/in-°F

@Temperature 68.0 °F
ASTM data
Deflection Temperature at 1.8 MPa (264 psi) 141 °C
286 °F
Unannealed; ASTM Data
Vicat Softening Point 160 °C
320 °F
Flammability, UL94 V-0

@Thickness 3.20 mm
V-0

@Thickness 0.126 in
Oxygen Index 38 %
38 %