Styron CALIBREâ„¢ 703-15 Polycarbonate Resin
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | Styron |
| Trade Name | CALIBRE™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styron CALIBREâ„¢ 703-15 Polycarbonate Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Overview: CALIBREâ„¢ 701-15 Series resins are formulated and produced to supply both clarity and enhanced ignition resistance. They do so while maintaining excellent physical properties and processability. The CLIBRE 701-15 series products are available in 2 additive packages: CLIBRE 701: Mold release. CALIBRE 7003: Mold release and UV stabilizer.Main Characteristics:Underwriters Laboratory Inc. (UL)Applications:Industrial switchesCircuit breakersPlugs, sockets and switchesStreet lightsSafety lightsReflectorsInformation provided by Styron
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183/A |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ISO 294-4 |
| Melt Flow | 15 g/10 min @Load 1.20 kg, Temperature 300 °C |
15 g/10 min @Load 2.65 lb, Temperature 572 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 66.0 MPa | 9570 psi | ISO 527-2/50 |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | ISO 527-2/50 |
| Elongation at Break | 120 % | 120 % | ISO 527-2/50 |
| Elongation at Yield | 6.0 % | 6.0 % | ISO 527-2/50 |
| Tensile Modulus | 2.30 GPa | 334 ksi | ISO 527-2/50 |
| Flexural Strength | 100 MPa | 14500 psi | 2.0 mm/min (3 point); ISO 178 |
| Flexural Modulus | 2.40 GPa | 348 ksi | 2.0 mm/min (3 point); ISO 178 |
| Izod Impact, Notched (ISO) | 83.0 kJ/m² @Temperature 23.0 °C |
39.5 ft-lb/in² @Temperature 73.4 °F |
ISO 180/A |
| Charpy Impact, Notched | 2.00 J/cm² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Hot Ball Pressure Test | 125 °C | 257 °F | IEC 60335-1 |
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C | 288 °F | Annealed; ISO 75-2/B |
| Deflection Temperature at 1.8 MPa (264 psi) | 122 °C | 252 °F | Unannealed; ISO 75-2/A |
| 139 °C | 282 °F | Annealed; ISO 75-2/A | |
| Vicat Softening Point | 147 °C | 297 °F | ISO 306/B50 |
| Flammability, UL94 | V-2 @Thickness 1.60 mm |
V-2 @Thickness 0.0630 in |
|
| V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 250 V @Thickness 2.00 mm |
250 V @Thickness 0.0787 in |
Solution A; IEC 60112 |