Styron CALIBREâ„¢ 5201-12 Polycarbonate Resin
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | Styron |
| Trade Name | CALIBRE™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styron CALIBREâ„¢ 5201-12 Polycarbonate Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Overview: CALIBREâ„¢ 5201-12 polycarbonate resin is 20% glass reinforced containing mold release for optimal processing. This resin exhibits high modulus and excellent dimensional stability. CALIBRE 5201-12 resin is typically used in electrical market applications. CALIBRE 5201-12 resin has undergone biocompatibility testing based on ISO 10993 (Biological Evaluation of Medical Devices) and is suitable for use in approved medical applications.Main Characteristics: Glass reinforcedIgnition resistantISO 10993 Applications:Medical applicationsHandheld surgical devicesPowdered medical devicesEquipment housingsElectrical componentsInformation provided by Styron
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | ISO 1183/B; ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in | ISO 294-4; ASTM D955 |
| Melt Flow | 12 g/10 min @Load 1.20 kg, Temperature 300 °C |
12 g/10 min @Load 2.65 lb, Temperature 572 °F |
ISO 1133; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 122 | 122 | ASTM D785 |
| Tensile Strength at Break | 82.7 MPa | 12000 psi | 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 82.7 MPa | 12000 psi | 50 mm/min; ISO 527-2/50; ASTM D638 |
| Elongation at Break | 2.6 % | 2.6 % | ISO 527-2/50 |
| 3.0 % | 3.0 % | 50 mm/min; ASTM D638 | |
| Elongation at Yield | 2.6 % | 2.6 % | 50 mm/min; ISO 527-2/50; ASTM D638 |
| Tensile Modulus | 5.17 GPa | 750 ksi | 50 mm/min; ISO 527-2/50; ASTM D638 |
| Flexural Strength | 148 MPa | 21500 psi | Method I (3 point load), 2.0 mm/min; ISO 178; ASTM D790 |
| Flexural Modulus | 4.82 GPa | 699 ksi | 2.0 mm/min; ISO 178 |
| 4.83 GPa | 701 ksi | Method I (3 point load), 2.0 mm/min; ASTM D790 | |
| Izod Impact, Notched | 1.10 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
2.06 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Dart Drop, Total Energy | 46.3 J @Thickness 3.20 mm |
34.1 ft-lb @Thickness 0.126 in |
3.39 m/sec; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 148 °C | 298 °F | Annealed; ISO 75-2/B |
| 148 °C | 298 °F | Annealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 138 °C | 280 °F | Unannealed; ISO 75-2/A; ASTM D648 |
| 142 °C | 288 °F | Annealed; ISO 75-2/A; ASTM D648 | |
| Vicat Softening Point | 158 °C | 316 °F | ISO 306/B50 |
| 159 °C @Load 5.10 kg |
318 °F @Load 11.2 lb |
Rate A (50°C/h); ASTM D1525 | |
| Flammability, UL94 | V-2 @Thickness 1.59 mm |
V-2 @Thickness 0.0626 in |
|
| V-0 @Thickness 3.05 mm |
V-0 @Thickness 0.120 in |