Styrolution Terluran® GP-25 ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded |
| Manufacturer | Styrolution |
| Trade Name | Terluran® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styrolution Terluran® GP-25 ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Terluran GP-25 is an easy-flow, general purpose injection molding grade with high resistance to impact and heat distortion; intended for a wide range of applications, particularly in the housings sector.Excellent colorabilityMedium flowGood impact resistanceGood heat distortion resistanceHigh quality surface finish and glossInformation provided by Styrolution
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.21 % @Temperature 23.0 °C |
0.21 % @Temperature 73.4 °F |
50% RH; ISO 62 |
| Water Absorption at Saturation | 0.95 % @Temperature 23.0 °C |
0.95 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ISO 294-4 |
| Melt Flow | 25 g/10 min @Load 10.0 kg, Temperature 220 °C |
25 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 99.0 MPa | 14400 psi | ISO 2039-1 |
| Tensile Strength, Yield | 44.0 MPa | 6380 psi | ISO 527 |
| Elongation at Break | 12 % | 12 % | ISO 527 |
| Elongation at Yield | 2.4 % | 2.4 % | ISO 527 |
| Tensile Modulus | 2.30 GPa | 334 ksi | ISO 527 |
| Flexural Strength | 65.0 MPa | 9430 psi | ISO 178 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
ISO 180/A |
| 22.0 kJ/m² @Temperature 23.0 °C |
10.5 ft-lb/in² @Temperature 73.4 °F |
ISO 180/A | |
| Charpy Impact Unnotched | 9.00 J/cm² @Temperature -30.0 °C |
42.8 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| 12.5 J/cm² @Temperature 23.0 °C |
59.5 ft-lb/in² @Temperature 73.4 °F |
ISO 179 | |
| Charpy Impact, Notched | 0.700 J/cm² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| 1.90 J/cm² @Temperature 23.0 °C |
9.04 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 80.0 - 110 µm/m-°C | 44.4 - 61.1 µin/in-°F | ISO 11359 |
| Thermal Conductivity | 0.170 W/m-K | 1.18 BTU-in/hr-ft²-°F | DIN 52612-1 |
| Deflection Temperature at 0.46 MPa (66 psi) | 97.0 °C | 207 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 93.0 °C | 199 °F | ISO 75 |
| Vicat Softening Point | 96.0 °C @Load 5.10 kg |
205 °F @Load 11.2 lb |
50°C/h; ISO 306 |
| 103 °C @Load 1.02 kg |
217 °F @Load 2.25 lb |
50°C/h; ISO 306 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Yellow Index | 15 % | 15 % | DIN 52912-1 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 220 - 260 °C | 428 - 500 °F | ISO 294 |
| Mold Temperature | 30.0 - 60.0 °C | 86.0 - 140 °F | ISO 294 |
| Injection Velocity | 200 mm/sec | 7.87 in/sec | ISO 294 |
| Drying Temperature | 80.0 °C @Time 7200 - 14400 sec |
176 °F @Time 2.00 - 4.00 hour |