Styrolution Terblend® N NM-11 ABS/PA6 (Conditioned)

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS)/Nylon Blend , Nylon
Manufacturer Styrolution
Trade Name Terblend®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Styrolution Terblend® N NM-11 ABS/PA6 (Conditioned).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Terblend N NM-11 is an ABS/PA6 blend combining very high impact strength, even at low temperatures, with an excellent processability and surface appearance.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS.
Physical Properties Metric English Comments
Density 1.07 g/cc
0.0387 lb/in³
dry; ISO 1183
Moisture Absorption at Equilibrium 1.3 %
1.3 %
beginning dry (23°C/50% R.H.); ISO 62
Melt Flow 18 g/10 min

@Load 10.0 kg,
Temperature 240 °C
18 g/10 min

@Load 22.0 lb,
Temperature 464 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 30.0 MPa
4350 psi
0.2 in/min; ASTM Test
Tensile Strength, Yield 32.0 MPa
4640 psi
2 in/min; ASTM Test
34.0 MPa
4930 psi
50mm/min; ISO 527
Elongation at Break >= 50 %
>= 50 %
50mm/min, Nominal strain; ISO 527
>= 100 %
>= 100 %
0.2 in/min; ASTM Test
Elongation at Yield 5.5 %
5.5 %
50mm/min; ISO 527
Tensile Modulus 1.38 GPa
200 ksi
ASTM Test
1.60 GPa
232 ksi
1mm/min; ISO 527
Izod Impact, Notched NB

@Thickness 3.17 mm
NB

@Thickness 0.125 in
ASTM Test
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+11 ohm-cm
>= 1.00e+11 ohm-cm
IEC 60093
Dielectric Constant 3.3

@Frequency 1.00e+6 Hz
3.3

@Frequency 1.00e+6 Hz
IEC 60250
Dielectric Strength 38.0 kV/mm
965 kV/in
IEC 60243-1
Dissipation Factor 0.055

@Frequency 1.00e+6 Hz
0.055

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 600 V
600 V
IEC 60112
Descriptive Properties Value Comments
Commercial Status Active America
Primary Processing Technique Injection Molding
UL.UL-C Yes