Styrolution Terblend® N NG-04 20% Glass Filled ABS/PA6 (Dry)

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS)/Nylon Blend, Glass Reinforced , Nylon
Manufacturer Styrolution
Trade Name Terblend®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Styrolution Terblend® N NG-04 20% Glass Filled ABS/PA6 (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Terblend N NG-04 is a glass fibre reinforced ABS/PA6 blend with excellent dimensional stability, low mold shrinkage and high heat resistance.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS.
Physical Properties Metric English Comments
Density 1.20 g/cc
0.0434 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 1.1 %
1.1 %
23°C/50% R.H.; ISO 62
Melt Flow 11 g/10 min

@Load 10.0 kg,
Temperature 240 °C
11 g/10 min

@Load 22.0 lb,
Temperature 464 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 73.0 MPa
10600 psi
0.2 in/min; ASTM Test
115 MPa

@Temperature -40.0 °C
16700 psi

@Temperature -40.0 °F
ISO Data
Tensile Strength, Ultimate 80.0 MPa
11600 psi
5mm/min; ISO 527
Tensile Strength, Yield 76.0 MPa
11000 psi
2 in/min; ASTM Test
37.0 MPa

@Temperature 80.0 °C
5370 psi

@Temperature 176 °F
ISO Data
Elongation at Break 3.0 %
3.0 %
0.2 in/min; ASTM Test
3.2 %
3.2 %
5mm/min; ISO 527
3.3 %

@Temperature -40.0 °C
3.3 %

@Temperature -40.0 °F
ISO Data
Elongation at Yield 5.9 %

@Temperature 80.0 °C
5.9 %

@Temperature 176 °F
ISO Data
Tensile Modulus 5.03 GPa
730 ksi
ASTM Test
5.40 GPa
783 ksi
1mm/min; ISO 527
Flexural Strength 115 MPa
16700 psi
ISO Data
Flexural Modulus 4.50 GPa
653 ksi
ISO Data
Izod Impact, Notched (ISO) 12.0 kJ/m²
5.71 ft-lb/in²
ISO Test
Charpy Impact Unnotched 5.00 J/cm²
23.8 ft-lb/in²
ISO 179
4.50 J/cm²

@Temperature -30.0 °C
21.4 ft-lb/in²

@Temperature -22.0 °F
ISO 179
Charpy Impact, Notched 1.40 J/cm²
6.66 ft-lb/in²
ISO 179
0.700 J/cm²

@Temperature -30.0 °C
3.33 ft-lb/in²

@Temperature -22.0 °F
ISO 179
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 40.0 µm/m-°C
22.2 µin/in-°F
ISO 11359
Deflection Temperature at 0.46 MPa (66 psi) 171 °C
340 °F
ASTM Test
174 °C
345 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 102 °C
215 °F
ASTM Test
104 °C
219 °F
ISO 75
Vicat Softening Point 114 °C
237 °F
(50 °C/h / 50N) - B/50; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
HB

@Thickness 3.20 mm
HB

@Thickness 0.126 in
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+13 ohm-cm
>= 1.00e+13 ohm-cm
IEC 60093
Dielectric Constant 2.9

@Frequency 1.00e+6 Hz
2.9

@Frequency 1.00e+6 Hz
IEC 60250
3.6

@Frequency 100 Hz
3.6

@Frequency 100 Hz
IEC 60250
Dielectric Strength 40.0 kV/mm
1020 kV/in
IEC 60243-1
Dissipation Factor 0.013

@Frequency 1.00e+6 Hz
0.013

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 600 V
600 V
IEC 60112
Processing Properties Metric English Comments
Melt Temperature 265 °C
509 °F
Injection molding
Injection Velocity 65.0 mm/sec
2.56 in/sec
Injection molding
Descriptive Properties Value Comments
Commercial Status Active America
Primary Processing Technique Injection Molding
UL.UL-C Yes