Styrolution Terblend® N NG-02 8% Glass Filled ABS/PA6 (Dry)

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS)/Nylon Blend, Glass Reinforced , Nylon
Manufacturer Styrolution
Trade Name Terblend®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Styrolution Terblend® N NG-02 8% Glass Filled ABS/PA6 (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Terblend N NG-02 is a glass fibre reinforced ABS/PA6 blend with excellent dimensional stability, high impact strength and good surface appearance.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS.
Physical Properties Metric English Comments
Density 1.12 g/cc
0.0405 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 1.3 %
1.3 %
23°C/50% R.H.; ISO 62
Melt Flow 14 g/10 min

@Load 10.0 kg,
Temperature 240 °C
14 g/10 min

@Load 22.0 lb,
Temperature 464 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 50.0 MPa
7250 psi
0.2 in/min; ASTM Test
Tensile Strength, Ultimate 55.0 MPa
7980 psi
5mm/min; ISO 527
Tensile Strength, Yield 53.0 MPa
7690 psi
2 in/min; ASTM Test
Elongation at Break 3.5 %
3.5 %
5mm/min; ISO 527
5.0 %
5.0 %
0.2 in/min; ASTM Test
Tensile Modulus 3.10 GPa
450 ksi
ASTM Test
3.20 GPa
464 ksi
1mm/min; ISO 527
Flexural Strength 80.0 MPa
11600 psi
ISO Data
Flexural Modulus 2.80 GPa
406 ksi
ISO Data
Izod Impact, Notched (ISO) 10.0 kJ/m²
4.76 ft-lb/in²
ISO Test
Charpy Impact Unnotched 4.50 J/cm²
21.4 ft-lb/in²
ISO 179
4.00 J/cm²

@Temperature -30.0 °C
19.0 ft-lb/in²

@Temperature -22.0 °F
ISO 179
Charpy Impact, Notched 1.20 J/cm²
5.71 ft-lb/in²
ISO 179
0.600 J/cm²

@Temperature -30.0 °C
2.86 ft-lb/in²

@Temperature -22.0 °F
ISO 179
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 60.0 µm/m-°C
33.3 µin/in-°F
ISO 11359
Deflection Temperature at 0.46 MPa (66 psi) 109 °C
228 °F
ASTM Test
110 °C
230 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 87.8 °C
190 °F
ASTM Test
90.0 °C
194 °F
ISO 75
Vicat Softening Point 108 °C
226 °F
(50 °C/h / 50N) - B/50; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
HB

@Thickness 3.20 mm
HB

@Thickness 0.126 in
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+13 ohm-cm
>= 1.00e+13 ohm-cm
IEC 60093
Dielectric Constant 2.9

@Frequency 1.00e+6 Hz
2.9

@Frequency 1.00e+6 Hz
IEC 60250
3.4

@Frequency 100 Hz
3.4

@Frequency 100 Hz
IEC 60250
Dielectric Strength 40.0 kV/mm
1020 kV/in
IEC 60243-1
Dissipation Factor 0.013

@Frequency 1.00e+6 Hz
0.013

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 600 V
600 V
IEC 60112
Processing Properties Metric English Comments
Melt Temperature 265 °C
509 °F
Injection molding
Injection Velocity 65.0 mm/sec
2.56 in/sec
Injection molding
Descriptive Properties Value Comments
Commercial Status Active America
Primary Processing Technique Injection Molding
UL.UL-C Yes