Styrolution PS 576H HIPS
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified |
| Manufacturer | Styrolution |
| Trade Name | PS |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styrolution PS 576H HIPS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Styrolution PS 576H is a high gloss, high impact polystyrene with a good flow and good heat resistance.High gloss HIPSGood flow and heat resistanceHIPS with good balance of mechanical properties and surface glossInformation provided by Styrolution
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | <= 0.10 % @Temperature 23.0 °C |
<= 0.10 % @Temperature 73.4 °F |
50% RH; ISO 62 |
| Water Absorption at Saturation | <= 0.10 % @Temperature 23.0 °C |
<= 0.10 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ISO 294-4 |
| Melt Flow | 5.5 g/10 min @Load 5.00 kg, Temperature 200 °C |
5.5 g/10 min @Load 11.0 lb, Temperature 392 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 83.0 MPa | 12000 psi | ISO 2039-1 |
| Tensile Strength, Yield | 30.0 MPa | 4350 psi | ISO 527 |
| Elongation at Break | 30 % | 30 % | ISO 527 |
| Elongation at Yield | 1.6 % | 1.6 % | ISO 527 |
| Tensile Modulus | 2.05 GPa | 297 ksi | ISO 527 |
| Flexural Strength | 44.0 MPa | 6380 psi | ISO 178 |
| Flexural Modulus | 2.10 GPa | 305 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | ISO 180/A |
| Charpy Impact Unnotched | 7.00 J/cm² @Temperature -30.0 °C |
33.3 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| 12.0 J/cm² @Temperature 23.0 °C |
57.1 ft-lb/in² @Temperature 73.4 °F |
ISO 179 | |
| Charpy Impact, Notched | 1.30 J/cm² | 6.19 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 100 µm/m-°C | 55.6 µin/in-°F | ISO 11359 |
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 78.0 °C | 172 °F | ISO 75 |
| Vicat Softening Point | 90.0 °C @Load 5.10 kg |
194 °F @Load 11.2 lb |
50°C/h; ISO 306 |
| 98.0 °C @Load 1.02 kg |
208 °F @Load 2.25 lb |
50°C/h; ISO 306 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 70 % | 70 % | Specular Gloss, 60°; ASTM D 523 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+18 ohm-cm | >= 1.00e+18 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+13 ohm | >= 1.00e+13 ohm | IEC 60093 |
| Dielectric Constant | 2.5 @Frequency 100 Hz |
2.5 @Frequency 100 Hz |
IEC 60250 |
| Dielectric Strength | 155 kV/mm @Thickness 1.50 mm |
3940 kV/in @Thickness 0.0591 in |
Short Time; IEC 60243-1 |
| Dissipation Factor | 0.00040 @Frequency 1.00e+6 Hz |
0.00040 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 180 - 260 °C | 356 - 500 °F | ISO 294 |
| Mold Temperature | 10.0 - 60.0 °C | 50.0 - 140 °F | ISO 294 |
| Injection Velocity | 200 mm/sec | 7.87 in/sec | ISO 294 |
Users viewing this material also viewed the following:
- Plastcom PLASTAMID® 6 BT N 29 B PA6
- Nye Lubricants UniFlor 8771R (UF) Synthetic Oil
- 3M Dyneon™ PFA 6503 A EPC Perfluoroalkoxy Fluorothermoplastic (discontinued **)
- 3M Dyneon™ CC155 Custom Fluoropolymer Compound (discontinued **)
- LATI Latiohm 73/23-10 CNT POM
- SABIC Innovative Plastics NORYL GFN1V PPE+HIPS (Europe-Africa-Middle East)
- A. Schulman POLYFORT™ PP 3726
- CPC - Vycom PROTEC® Homopolymer Polypropylene
- Covestro Makrolon® LQ2687 Polycarbonate
Copyright © lookpolymers.com All Rights Reserved