Stellar Canada CERAMITE® SFR Wear Resistant Castable

Category Ceramic , Oxide , Silicon Oxide
Manufacturer Stellar Canada
Trade Name CERAMITE®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Stellar Canada CERAMITE® SFR Wear Resistant Castable.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ceramite is a family of wear resistant castables with a unique combination of high wear resistance, thermal resistance and mechanical strength. Ceramite is produced and supplied to end users world wide, both as mortars and as various precast components. Ceramite can easily be mixed, cast and shaped in any size and is thus comfortably to work with in-situ. Ceramite can be used in within a wide range of temperatures and applications exposed to thermal shock conditions in industries like for example aluminum, cement and ferro.Applications: Floor Tile, Hearth/Furnace Tile, Furnace Sills & Doors, Lintels, Pipe and Duct Linings, Feed Tubes, Troughs/Launders, Ladles, Dampers, Nozzle Blasters, Crucible Linings, Vortex, Burner Tip Cooler Plates, Nose Ring, Electrical Insulation, Cold Wear AreasSpecific Notes on This Grade: A castable combining good mechanical and thermal properties. Extremely low thermal expansion. Mainly used in aluminum and zinc industries. References al launders, crucibles and other areas in contact with molten metal.Information provided by Stellar Canada.
Physical Properties Metric English Comments
Bulk Density 2.07 g/cc
0.0747 lb/in³
As Placed
Porosity 10.4 %
10.4 %
Apparent
Mechanical Properties Metric English Comments
Modulus of Rupture 0.008998 GPa
1.305 ksi
Hot, prefired at 1832°F/24 hours (1000°C)
Flexural Strength 3.98 MPa

@Temperature 1000 °C
577 psi

@Temperature 1832 °F
after Firing; ASTM-349
5.27 MPa

@Temperature 850.0 °C
764 psi

@Temperature 1562 °F
after Firing; ASTM-349
6.20 MPa

@Temperature 500 °C
899 psi

@Temperature 932 °F
after Firing; ASTM-349
Compressive Strength 108.00 MPa
15664 psi
Cold Crushing after 1560°F
80.234 MPa

@Temperature 1000 °C
11637 psi

@Temperature 1830 °F
after Firing; ASTM C-349
92.190 MPa

@Temperature 850 °C
13371 psi

@Temperature 1560 °F
after Firing; ASTM C-349
95.161 MPa

@Temperature 20.0 °C
13802 psi

@Temperature 68.0 °F
after 7 days
112.89 MPa

@Temperature 500 °C
16374 psi

@Temperature 932 °F
after Firing; ASTM C-349
Thermal Properties Metric English Comments
Thermal Conductivity 1.02 W/m-K

@Temperature 300 °C
7.07 BTU-in/hr-ft²-°F

@Temperature 572 °F
1.25 W/m-K

@Temperature 600.0 °C
8.67 BTU-in/hr-ft²-°F

@Temperature 1112 °F
1.458 W/m-K

@Temperature 900.0 °C
10.12 BTU-in/hr-ft²-°F

@Temperature 1652 °F
Maximum Service Temperature, Air 999 °C
1830 °F
Component Elements Properties Metric English Comments
Al2O3 21 %
21 %
CaO 6.3 %
6.3 %
Fe2O3 0.070 %
0.070 %
K2O 0.020 %
0.020 %
MgO 0.010 %
0.010 %
Na2O 0.030 %
0.030 %
SiO2 73 %
73 %
Descriptive Properties Value Comments
Application Prefired
Precast Shapes