Stellar Canada CERAMITE® CSR Wear Resistant Castable

Category Ceramic , Carbide
Manufacturer Stellar Canada
Trade Name CERAMITE®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Stellar Canada CERAMITE® CSR Wear Resistant Castable.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ceramite is a family of wear resistant castables with a unique combination of high wear resistance, thermal resistance and mechanical strength. Ceramite is produced and supplied to end users world wide, both as mortars and as various precast components. Ceramite can easily be mixed, cast and shaped in any size and is thus comfortably to work with in-situ. Ceramite can be used in within a wide range of temperatures and applications exposed to thermal shock conditions in industries like for example aluminum, cement and ferro.Applications: Floor Tile, Hearth/Furnace Tile, Furnace Sills & Doors, Lintels, Pipe and Duct Linings, Feed Tubes, Troughs/Launders, Ladles, Dampers, Nozzle Blasters, Crucible Linings, Vortex, Burner Tip Cooler Plates, Nose Ring, Electrical Insulation, Cold Wear AreasSpecific Notes on This Grade: A castable with extreme abrasion resistance and high thermal conductivity. Used in the same industries as BKR in areas with high abrasion problems. References as lining material for pipes and bends, impact plates, lining of transportation systems, duct linings, crucible linings etc...Information provided by Stellar Canada.
Physical Properties Metric English Comments
Bulk Density 2.66 g/cc
0.0961 lb/in³
As Placed
Porosity 13.7 %
13.7 %
Apparent
Mechanical Properties Metric English Comments
Modulus of Rupture 0.02500 GPa
3.626 ksi
Hot, prefired at 1832°F/24 hours (1000°C)
Flexural Strength 11.9 MPa

@Temperature 1200 °C
1730 psi

@Temperature 2192 °F
after Firing; ASTM-349
16.40 MPa

@Temperature 850.0 °C
2379 psi

@Temperature 1562 °F
after Firing; ASTM-349
18.70 MPa

@Temperature 1000 °C
2712 psi

@Temperature 1832 °F
after Firing; ASTM-349
20.00 MPa

@Temperature 500 °C
2901 psi

@Temperature 932 °F
after Firing; ASTM-349
Compressive Strength 221.00 MPa
32054 psi
Cold Crushing after 1560°F
80.000 MPa

@Temperature 1200 °C
11603 psi

@Temperature 2190 °F
after Firing; ASTM C-349
112.00 MPa

@Temperature 1000 °C
16244 psi

@Temperature 1830 °F
after Firing; ASTM C-349
118.00 MPa

@Temperature 850 °C
17115 psi

@Temperature 1560 °F
after Firing; ASTM C-349
149.00 MPa

@Temperature 20.0 °C
21611 psi

@Temperature 68.0 °F
after 7 days
184.00 MPa

@Temperature 500 °C
26687 psi

@Temperature 932 °F
after Firing; ASTM C-349
Thermal Properties Metric English Comments
Thermal Conductivity 6.912 W/m-K

@Temperature 900.0 °C
47.97 BTU-in/hr-ft²-°F

@Temperature 1652 °F
7.268 W/m-K

@Temperature 600.0 °C
50.44 BTU-in/hr-ft²-°F

@Temperature 1112 °F
9.31 W/m-K

@Temperature 300 °C
64.6 BTU-in/hr-ft²-°F

@Temperature 572 °F
Maximum Service Temperature, Air 999 °C
1830 °F
Component Elements Properties Metric English Comments
Al2O3 16 %
16 %
CaO 6.3 %
6.3 %
Fe2O3 0.030 %
0.030 %
K2O 0.020 %
0.020 %
MgO 0.010 %
0.010 %
SiC 69 %
69 %
SiO2 8.0 %
8.0 %
Descriptive Properties Value Comments
Application Prefired
Precast Shapes