Star Plastics ABSHFL Molding Grade ABS High Flow

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded
Manufacturer Star Plastics, Inc
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Star Plastics ABSHFL Molding Grade ABS High Flow.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Star Plastics, Inc.
Physical Properties Metric English Comments
Specific Gravity 1.05 g/cc
1.05 g/cc
ASTM D792
Maximum Moisture Content 0.15
0.15
Linear Mold Shrinkage 0.0040 - 0.0080 cm/cm
0.0040 - 0.0080 in/in
ASTM D955
Melt Flow 8.0 g/10 min

@Load 3.80 kg,
Temperature 230 °C
8.0 g/10 min

@Load 8.38 lb,
Temperature 446 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 41.4 MPa
6000 psi
ASTM D638
Tensile Modulus 2.28 GPa
330 ksi
ASTM D638
Flexural Yield Strength 68.9 MPa
10000 psi
ASTM D790
Flexural Modulus 2.41 GPa
350 ksi
ASTM D790
Izod Impact, Notched 1.07 J/cm
2.00 ft-lb/in
73°F, 0.125 in.; ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 82.2 °C
180 °F
unannealed, .125in; ASTM D648
Flammability, UL94 HB
HB
Processing Properties Metric English Comments
Rear Barrel Temperature 188 - 218 °C
370 - 425 °F
Middle Barrel Temperature 204 - 232 °C
400 - 450 °F
Front Barrel Temperature 218 - 246 °C
425 - 475 °F
Nozzle Temperature 218 - 274 °C
425 - 525 °F
Melt Temperature 218 - 274 °C
425 - 525 °F
Mold Temperature 37.8 - 48.9 °C
100 - 120 °F
Drying Temperature 82.2 - 93.3 °C
180 - 200 °F
Dry Time 2 - 4 hour
2 - 4 hour
Back Pressure 0.172 - 0.689 MPa
25.0 - 100 psi
Screw Speed 25 - 75 rpm
25 - 75 rpm