Special Metals INCONEL® Alloy 601
| Category | Metal , Nonferrous Metal , Nickel Alloy , Superalloy |
| Manufacturer | Special Metals (includes the former Inco Alloys International Inc.) |
| Trade Name | INCONEL® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Special Metals INCONEL® Alloy 601.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
A nickel-chromium alloy with an addition of aluminum for outstanding resistance to oxidation and other forms of high-temperature corrosion. It also has high mechanical properties at elevated temperatures. Used for industrial furnaces; heat-treating equipment such as baskets, muffles, and retorts; petrochemical and other process equipment; and gas-turbine components. Standard product forms are round, flats, forging stock, pipe, tube, plate, sheet, strip, and wire.Data provided by the manufacturer, Special Metals.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 8.11 g/cc | 0.293 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 620 MPa @Temperature 550 °C |
89900 psi @Temperature 1020 °F |
Solution Annealed prior to test |
| 760 MPa @Temperature 23.0 °C |
110000 psi @Temperature 73.4 °F |
||
| Tensile Strength, Yield | 450 MPa @Strain 0.200 % |
65300 psi @Strain 0.200 % |
Solution Annealed. Value at room temperature |
| 330 MPa @Strain 0.200 %, Temperature 550 °C |
47900 psi @Strain 0.200 %, Temperature 1020 °F |
Solution Annealed prior to test | |
| Elongation at Break | 42 % | 42 % | Solution Annealed |
| 32 % @Temperature 550 °C |
32 % @Temperature 1020 °F |
Solution Annealed prior to test. |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 13.75 µm/m-°C @Temperature 20.0 - 100 °C |
7.639 µin/in-°F @Temperature 68.0 - 212 °F |
|
| Specific Heat Capacity | 0.448 J/g-°C | 0.107 BTU/lb-°F | |
| Thermal Conductivity | 11.2 W/m-K | 77.7 BTU-in/hr-ft²-°F | |
| Melting Point | 1360 - 1411 °C | 2480 - 2572 °F | |
| Solidus | 1360 °C | 2480 °F | |
| Liquidus | 1411 °C | 2572 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Aluminum, Al | 1.0 - 1.7 % | 1.0 - 1.7 % | |
| Carbon, C | <= 0.10 % | <= 0.10 % | |
| Chromium, Cr | 21 - 25 % | 21 - 25 % | |
| Copper, Cu | <= 1.0 % | <= 1.0 % | |
| Iron, Fe | 13 % | 13 % | As remainder |
| Manganese, Mn | <= 1.0 % | <= 1.0 % | |
| Nickel, Ni | 58 - 63 % | 58 - 63 % | |
| Silicon, Si | <= 0.50 % | <= 0.50 % | |
| Sulfur, S | <= 0.015 % | <= 0.015 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.000119 ohm-cm | 0.000119 ohm-cm | |
| Magnetic Permeability | 1.003 | 1.003 | at 200 oersted (15.9 kA/m) |
| Curie Temperature | <= -196 °C | <= -321 °F |