Special Metals INCONEL® 706 Precipitation Hardening Alloy, Hot Finished Rod, 2 Part Heat Treatment, 0.562 inch (14.3 mm) Diameter

Category Metal , Nonferrous Metal , Nickel Alloy , Superalloy , Iron Base
Manufacturer Special Metals (includes the former Inco Alloys International Inc.)
Trade Name INCONEL®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Special Metals INCONEL® 706 Precipitation Hardening Alloy, Hot Finished Rod, 2 Part Heat Treatment, 0.562 inch (14.3 mm) Diameter.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Tensile strength (ultimate and yield), shear strength, reduction of area, and elongation values reported here are typical for Hot Finished Rod, 2 Part Heat Treatment, 0.562 inch (14.3 mm) Diameter samples. Density and magnetic permeability are typical of precipitation hardened INCONEL® alloy 706. Other property values are typical of INCONEL® alloy 706.For tensile-limited applications, the alloy receives a two part heat treatment as follows: Solution treat 1700-1850°F (925-1010°C) for a time commensurate with section size, then air cool. Precipitation treatment 1350°F (730°C)/8 hr, furnace cool at 100°F (55°C)/hr to 1150°F (620°C)/8 hr, air cool.Data provided by the manufacturer, Special Metals.
Physical Properties Metric English Comments
Density 8.08 g/cc
0.292 lb/in³
Precipitation Hardened
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 1330 MPa
193000 psi
Tensile Strength, Yield 1090 MPa

@Strain 0.200 %
158000 psi

@Strain 0.200 %
Elongation at Break 21 %
21 %
Reduction of Area 55 %
55 %
Modulus of Elasticity 210 GPa
30500 ksi
Dynamic Method
Poissons Ratio 0.382
0.382
Calculated by mfr.
Shear Modulus 76.0 GPa
11000 ksi
Dynamic Method
Shear Strength 899.1 MPa
130400 psi
Thickness not reported for this value
Thermal Properties Metric English Comments
CTE, linear 13.46 µm/m-°C

@Temperature 24.0 - 100 °C
7.478 µin/in-°F

@Temperature 75.2 - 212 °F
Mean
15.08 µm/m-°C

@Temperature 24.0 - 300 °C
8.378 µin/in-°F

@Temperature 75.2 - 572 °F
Mean
15.59 µm/m-°C

@Temperature 24.0 - 500 °C
8.661 µin/in-°F

@Temperature 75.2 - 932 °F
Mean
16.42 µm/m-°C

@Temperature 21.0 - 700 °C
9.122 µin/in-°F

@Temperature 69.8 - 1290 °F
Mean
Specific Heat Capacity 0.444 J/g-°C
0.106 BTU/lb-°F
Thermal Conductivity 12.5 W/m-K
86.8 BTU-in/hr-ft²-°F
Melting Point 1334 - 1371 °C
2433 - 2500 °F
Solidus 1334 °C
2433 °F
Liquidus 1371 °C
2500 °F
Component Elements Properties Metric English Comments
Aluminum, Al <= 0.060 %
<= 0.060 %
Boron, B <= 0.0060 %
<= 0.0060 %
Carbon, C <= 0.30 %
<= 0.30 %
Chromium, Cr 14.5 - 17.5 %
14.5 - 17.5 %
Cobalt, Co <= 1.0 %
<= 1.0 %
Copper, Cu <= 0.35 %
<= 0.35 %
Iron, Fe 38 %
38 %
As remainder
Manganese, Mn <= 0.35 %
<= 0.35 %
Nickel, Ni 39 - 44 %
39 - 44 %
Including Cobalt
Niobium, Nb (Columbium, Cb) 2.5 - 3.3 %
2.5 - 3.3 %
Includes Ta
Phosphorous, P <= 0.020 %
<= 0.020 %
Silicon, Si <= 0.35 %
<= 0.35 %
Sulfur, S <= 0.015 %
<= 0.015 %
Titanium, Ti <= 0.40 %
<= 0.40 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.0000985 ohm-cm
0.0000985 ohm-cm
Magnetic Permeability 1.01
1.01
at 200 Oersted (15.9 kA/m);Annealed
Curie Temperature <= -78.0 °C
<= -108 °F