- Special Metals INCONEL® 706 Precipitation Hardening Alloy, Forged Disc, 3 Part Heat Treatment
Special Metals INCONEL® 706 Precipitation Hardening Alloy, Forged Disc, 3 Part Heat Treatment
| Category | Metal , Nonferrous Metal , Nickel Alloy , Superalloy , Iron Base |
| Manufacturer | Special Metals (includes the former Inco Alloys International Inc.) |
| Trade Name | INCONEL® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Special Metals INCONEL® 706 Precipitation Hardening Alloy, Forged Disc, 3 Part Heat Treatment.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Tensile strength (ultimate and yield), reduction of area, and elongation values reported here are typical for Forged Disc, 3 Part Heat Treatment samples. Density and magnetic permeability are typical of precipitation hardened INCONEL® alloy 706. Other property values are typical of INCONEL® alloy 706.For optimum creep and rupture properties, the alloy receives a three part heat treatment as follows: Solution treat 1700-1850°F (925-1010°C) for a time commensurate with section size, then air cool. Stabilizing treatment 1550°F (845°C)/3 hr, air cool. Precipitation treatment 1325°F (720°C)/8 hr, furnace cool at 100°F (55°C)/hr to 1150°F (620°C)/8 hr, air cool.Data provided by the manufacturer, Special Metals.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 8.08 g/cc | 0.292 lb/in³ | Precipitation Hardened |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 1245 MPa | 180500 psi | |
| Tensile Strength, Yield | 979 MPa @Strain 0.200 % |
142000 psi @Strain 0.200 % |
|
| Elongation at Break | 17 % | 17 % | |
| Reduction of Area | 19 % | 19 % | |
| Modulus of Elasticity | 210 GPa | 30500 ksi | Dynamic Method |
| Poissons Ratio | 0.382 | 0.382 | Calculated by mfr. |
| Shear Modulus | 76.0 GPa | 11000 ksi | Dynamic Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 13.46 µm/m-°C @Temperature 24.0 - 100 °C |
7.478 µin/in-°F @Temperature 75.2 - 212 °F |
Mean |
| 15.08 µm/m-°C @Temperature 24.0 - 300 °C |
8.378 µin/in-°F @Temperature 75.2 - 572 °F |
Mean | |
| 15.59 µm/m-°C @Temperature 24.0 - 500 °C |
8.661 µin/in-°F @Temperature 75.2 - 932 °F |
Mean | |
| 16.42 µm/m-°C @Temperature 21.0 - 700 °C |
9.122 µin/in-°F @Temperature 69.8 - 1290 °F |
Mean | |
| Specific Heat Capacity | 0.444 J/g-°C | 0.106 BTU/lb-°F | |
| Thermal Conductivity | 12.5 W/m-K | 86.8 BTU-in/hr-ft²-°F | |
| Melting Point | 1334 - 1371 °C | 2433 - 2500 °F | |
| Solidus | 1334 °C | 2433 °F | |
| Liquidus | 1371 °C | 2500 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Aluminum, Al | <= 0.060 % | <= 0.060 % | |
| Boron, B | <= 0.0060 % | <= 0.0060 % | |
| Carbon, C | <= 0.30 % | <= 0.30 % | |
| Chromium, Cr | 14.5 - 17.5 % | 14.5 - 17.5 % | |
| Cobalt, Co | <= 1.0 % | <= 1.0 % | |
| Copper, Cu | <= 0.35 % | <= 0.35 % | |
| Iron, Fe | 38 % | 38 % | As remainder |
| Manganese, Mn | <= 0.35 % | <= 0.35 % | |
| Nickel, Ni | 39 - 44 % | 39 - 44 % | Including Cobalt |
| Niobium, Nb (Columbium, Cb) | 2.5 - 3.3 % | 2.5 - 3.3 % | Includes Ta |
| Phosphorous, P | <= 0.020 % | <= 0.020 % | |
| Silicon, Si | <= 0.35 % | <= 0.35 % | |
| Sulfur, S | <= 0.015 % | <= 0.015 % | |
| Titanium, Ti | <= 0.40 % | <= 0.40 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.0000985 ohm-cm | 0.0000985 ohm-cm | |
| Magnetic Permeability | 1.01 | 1.01 | at 200 Oersted (15.9 kA/m);Annealed |
| Curie Temperature | <= -78.0 °C | <= -108 °F |