Solvay Technyl® B 50H1 Nylon 66/6, Flame Retardant, EH0

Category Polymer , Thermoplastic , Nylon , Nylon 6/66 , Nylon 66/6, Unreinforced
Manufacturer Solvay
Trade Name Technyl®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Technyl® B 50H1 Nylon 66/6, Flame Retardant, EH0.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Flame retardant copolyamide 66/6, unreinforced, heat stabilized, for injection molding.This phosphorus and halogen free flame retardant grade, UL 94 VO (0.4 mm), offers excellent filling qualities and with good stiffness. It is particularly suitable for molding insulating parts for electrical components on board materials for use in tunnels, satisfying specification n°3 of the standard "Fire and Smoke" NF-F16102, and on components for electrical connections : junction blocks, terminal blocks, connectors.This product is available in natural, black, and in colors on request.Glow wire test thick. 1,6 mm, IEC 695-2-1, is 960°C. Glow wire test thick. 1,6 mm: no flame, IEC 695-2-1, is 650°C. Glow wire test thick. 0,8 mm: c
Physical Properties Metric English Comments
Density 1.16 g/cc
0.0419 lb/in³
ISO 1183-A
Water Absorption 1.1 %
1.1 %
24 hours in water at 23°C; ISO 62.
Linear Mold Shrinkage 0.011 cm/cm
0.011 in/in
RHODIA-EP
Linear Mold Shrinkage, Transverse 0.010 cm/cm
0.010 in/in
RHODIA-EP
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 80.0 MPa
11600 psi
ISO 527
Tensile Strength, Yield 80.0 MPa
11600 psi
ISO 527
Elongation at Break 5.0 %
5.0 %
ISO 527
Elongation at Yield 5.0 %
5.0 %
ISO 527
Tensile Modulus 3.70 GPa
537 ksi
ISO 527
Flexural Yield Strength 105 MPa
15200 psi
ISO 178
Flexural Modulus 3.50 GPa
508 ksi
ISO 178
Izod Impact Resistance 0.300 J/cm²
1.43 ft-lb/in²
ISO 180
Charpy Impact Unnotched 6.00 J/cm²
28.6 ft-lb/in²
ISO 179/1EA-1993
Charpy Impact, Notched 0.300 J/cm²
1.43 ft-lb/in²
ISO 179/1EA-1993
Thermal Properties Metric English Comments
CTE, linear 65.0 µm/m-°C

@Temperature 23.0 - 85.0 °C
36.1 µin/in-°F

@Temperature 73.4 - 185 °F
ASTM E831
Melting Point 242 °C
468 °F
ISO 3146-C
Deflection Temperature at 1.8 MPa (264 psi) 85.0 °C
185 °F
ISO 75-2
Flammability, UL94 V-0

@Thickness 0.400 mm
V-0

@Thickness 0.0157 in
ISO 1210/UL 94
V-0

@Thickness 0.800 mm
V-0

@Thickness 0.0315 in
ISO 1210/UL 94
V-0

@Thickness 1.60 mm
V-0

@Thickness 0.0630 in
ISO 1210/UL 94
Oxygen Index 37 %
37 %
ISO 4589
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 93
Surface Resistance 1.00e+15 ohm
1.00e+15 ohm
IEC 93
Dielectric Constant 3.6

@Frequency 1e+6 Hz
3.6

@Frequency 1e+6 Hz
IEC 250
Dielectric Strength 34.0 kV/mm
864 kV/in
IEC 243-1
Dissipation Factor 0.020

@Frequency 1e+6 Hz
0.020

@Frequency 1e+6 Hz
IEC 250
Comparative Tracking Index 600 V
600 V
IEC 112
Processing Properties Metric English Comments
Rear Barrel Temperature 240 - 250 °C
464 - 482 °F
Middle Barrel Temperature 245 - 255 °C
473 - 491 °F
Front Barrel Temperature 250 - 260 °C
482 - 500 °F