Solvay Technyl® A 60G1 V25 25% Glass Reinforced Nylon 66, Flame Retardant
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Technyl® A 60G1 V25 25% Glass Reinforced Nylon 66, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
This Red Phosphorous and Halogen free flame retardant grade, combines excellent all-round mechanical properties with outstanding flame retardancy (UL 5VA at 1.6mm) and electrical performance. This product is ideally suited for industrial controls and power distribution applications such as MCBs and contactors. The long term thermal performance of this grade also make it ideal for underhood auto applications where it can withstand temperatures of 160°C for over 6000hrs.Information provided by Rhodia; Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in³ | ISO 1183-A |
| Water Absorption | 0.83 % @Time 86400 sec |
0.83 % @Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0045 cm/cm | 0.0045 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0085 cm/cm | 0.0085 in/in | ISO 294-4 |
| 0.0090 cm/cm | 0.0090 in/in | Rhodia EP test |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 92.0 MPa | 13300 psi | Conditioned; ISO 527 Type 1 A |
| 147 MPa | 21300 psi | DAM; ISO 527 Type 1 A | |
| Elongation at Break | 3.1 % | 3.1 % | DAM; ISO 527 Type 1 A |
| 5.2 % | 5.2 % | Conditioned; ISO 527 Type 1 A | |
| Tensile Modulus | 6.20 GPa | 899 ksi | Conditioned; ISO 527 Type 1 A |
| 9.50 GPa | 1380 ksi | DAM; ISO 527 Type 1 A | |
| Charpy Impact Unnotched | 6.50 J/cm² | 30.9 ft-lb/in² | DAM; ISO 179/1eU |
| 8.50 J/cm² | 40.5 ft-lb/in² | Conditioned; ISO 179/1eU | |
| 6.00 J/cm² @Temperature -30.0 °C |
28.6 ft-lb/in² @Temperature -22.0 °F |
DAM; ISO 179/fU | |
| Charpy Impact, Notched | 0.760 J/cm² | 3.62 ft-lb/in² | DAM; ISO 179/1eA |
| 0.910 J/cm² | 4.33 ft-lb/in² | Conditioned; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 263 °C | 505 °F | ISO 11357 |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | DAM; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 116 °C | 240 °F | DAM; ISO 75/Af |
| Flammability, UL94 | V-0 @Thickness 0.787 mm |
V-0 @Thickness 0.0310 in |
DAM; ISO 1210/UL94 |
| V-0 @Thickness 3.17 mm |
V-0 @Thickness 0.125 in |
DAM; ISO 1210/UL94 | |
| Oxygen Index | 33 % | 33 % | DAM; ISO 4589 |
| Glow Wire Test | 775 °C @Thickness 3.20 mm |
1430 °F @Thickness 0.126 in |
Ignition Temperature; DAM; IEC 60695-2-13 |
| 775 °C @Thickness 1.60 mm |
1430 °F @Thickness 0.0630 in |
Ignition Temperature; DAM; IEC 60695-2-13 | |
| 960 °C @Thickness 0.800 mm |
1760 °F @Thickness 0.0315 in |
Flammability Index; DAM; IEC 60695-2-12 | |
| 960 °C @Thickness 1.60 mm |
1760 °F @Thickness 0.0630 in |
Flammability Index; DAM; IEC 60695-2-12 | |
| 960 °C @Thickness 3.20 mm |
1760 °F @Thickness 0.126 in |
Flammability Index; DAM; IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+9 ohm-cm | 1.00e+9 ohm-cm | Conditioned; IEC 60093 |
| 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | DAM; IEC 60093 | |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | Conditioned; IEC 60093 |
| Dielectric Constant | 3.7 | 3.7 | DAM; IEC 60250 |
| 4.5 | 4.5 | Conditioned; IEC 60250 | |
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | DAM; IEC 60243 |
| Comparative Tracking Index | 600 V | 600 V | Conditioned; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 260 - 270 °C | 500 - 518 °F | |
| Middle Barrel Temperature | 260 - 270 °C | 500 - 518 °F | |
| Front Barrel Temperature | 260 - 270 °C | 500 - 518 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |