Solvay TECHNYLSTARâ„¢ S 60G1 V30 PA6, 30% glass filled, DRY

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled
Manufacturer Solvay
Trade Name TECHNYLSTAR™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay TECHNYLSTARâ„¢ S 60G1 V30 PA6, 30% glass filled, DRY.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: TECHNYLSTARâ„¢ S 60G1 V30 is a reinforced 30% GF organophosphorous flame retarded grade based on a patented high flow polyamide 6 resin (TechnylStar). This product is heat stabilized and provides optimized injection moulding performance. This product is available in natural, grey & black colors as standard and can be made in other specific colors upon request.Benefits: This product offers excellent flame retardancy properties (UL 94, 5VA, GWIT) combined with best in class processing, mechanical and electrical performance.Available in: Asia Pacific, Europe, Latin America and North AmericaRegulations compliance: Grades produced or imported in Europe comply with directive 453/2010/EC, which amends REACH directive 1907/2006/EC. This grade complies with RoHS directive 2002/95/EC. Unless specified, this grade is not suitable for food contact, medical devices or toy applications.Applications: This product is ideally suited for power distribution, industrial control and appliance applications such as MCBs and contactors, as well as being able to be used in many varied thin wall applications where its high flow polymer base enables it to achieve a UL94 V-0 rating down to a 0.4mm wall thickness.Information provided by Rhodia, Rhodia has been acquired by Solvay.
Physical Properties Metric English Comments
Density 1.42 g/cc
0.0513 lb/in³
ISO 1183/A
Water Absorption 0.90 %

@Temperature 23.0 °C,
Time 86400 sec
 0.90 %

@Temperature 73.4 °F,
Time 24.0 hour
 ISO 62
Viscosity 50 cP

@Shear Rate 1000 1/s,
Temperature 270 °C
 50 cP

@Shear Rate 1000 1/s,
Temperature 518 °F
120 cP

@Shear Rate 1000 1/s,
Temperature 250 °C
 120 cP

@Shear Rate 1000 1/s,
Temperature 482 °F
120 cP

@Shear Rate 100 1/s,
Temperature 270 °C
 120 cP

@Shear Rate 100 1/s,
Temperature 518 °F
200 cP

@Shear Rate 1000 1/s,
Temperature 230 °C
 200 cP

@Shear Rate 1000 1/s,
Temperature 446 °F
200 cP

@Shear Rate 100 1/s,
Temperature 250 °C
 200 cP

@Shear Rate 100 1/s,
Temperature 482 °F
300 cP

@Shear Rate 100 1/s,
Temperature 230 °C
 300 cP

@Shear Rate 100 1/s,
Temperature 446 °F
Linear Mold Shrinkage 0.0057 cm/cm
0.0057 in/in
Isotropy
Linear Mold Shrinkage, Flow 0.0040 cm/cm
0.0040 in/in
Linear Mold Shrinkage, Transverse 0.0070 cm/cm
0.0070 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 147 MPa
21300 psi
ISO 527 Type 1A
155 MPa
22500 psi
ASTM D638
Tensile Stress 90.0 MPa

@Strain 1.00 %
 13100 psi

@Strain 1.00 %
135 MPa

@Strain 2.00 %
 19600 psi

@Strain 2.00 %
Elongation at Break 2.4 %
2.4 %
ISO 527 Type 1A
2.5 %
2.5 %
ASTM D638
Tensile Modulus 11.8 GPa
1710 ksi
ISO 527 Type 1A
Flexural Strength 240 MPa
34800 psi
ASTM D790
243 MPa
35200 psi
ISO 178
Flexural Modulus 10.5 GPa
1520 ksi
ASTM D790
10.7 GPa
1550 ksi
ISO 178
Izod Impact, Notched 1.20 J/cm
2.25 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 10.0 kJ/m²
4.76 ft-lb/in²
ISO 180/1eA
Izod Impact, Unnotched (ISO) 54.0 kJ/m²
25.7 ft-lb/in²
ISO 180/1eU
Charpy Impact Unnotched 6.00 J/cm²
28.6 ft-lb/in²
ISO 179/1eU
Charpy Impact, Notched 0.960 J/cm²
4.57 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 222 °C
432 °F
ISO 11357
Deflection Temperature at 1.8 MPa (264 psi) 205 °C
401 °F
ISO 75/Af
UL RTI, Electrical 65.0 °C

@Thickness 0.400 mm
 149 °F

@Thickness 0.0157 in
130 °C

@Thickness 0.750 mm
 266 °F

@Thickness 0.0295 in
130 °C

@Thickness 1.50 mm
 266 °F

@Thickness 0.0591 in
130 °C

@Thickness 3.00 mm
 266 °F

@Thickness 0.118 in
130 °C

@Thickness 1.50 mm
 266 °F

@Thickness 0.0591 in
 NC,BK
130 °C

@Thickness 3.00 mm
 266 °F

@Thickness 0.118 in
 NC,BK
UL RTI, Mechanical with Impact 65.0 °C

@Thickness 0.400 mm
 149 °F

@Thickness 0.0157 in
105 °C

@Thickness 0.750 mm
 221 °F

@Thickness 0.0295 in
115 °C

@Thickness 1.50 mm
 239 °F

@Thickness 0.0591 in
115 °C

@Thickness 3.00 mm
 239 °F

@Thickness 0.118 in
115 °C

@Thickness 1.50 mm
 239 °F

@Thickness 0.0591 in
 NC, BK
115 °C

@Thickness 3.00 mm
 239 °F

@Thickness 0.118 in
 NC, BK
Flammability, UL94 V-0

@Thickness 0.380 mm
 V-0

@Thickness 0.0150 in
 1210
V-0

@Thickness 0.800 mm
 V-0

@Thickness 0.0315 in
 1210
V-0

@Thickness 1.60 mm
 V-0

@Thickness 0.0630 in
 1210
V-0

@Thickness 3.20 mm
 V-0

@Thickness 0.126 in
 1210
Oxygen Index 35 %
35 %
ISO 4589
Glow Wire Test 775 °C

@Thickness 0.800 mm
 1430 °F

@Thickness 0.0315 in
 ignition temperature; ISO 60695-2-13
800 °C

@Thickness 1.60 mm
 1470 °F

@Thickness 0.0630 in
 ignition temperature; ISO 60695-2-13
960 °C

@Thickness 0.800 mm
 1760 °F

@Thickness 0.0315 in
 ISO 60695-2-12
960 °C

@Thickness 1.60 mm
 1760 °F

@Thickness 0.0630 in
 ISO 60695-2-12
960 °C

@Thickness 3.20 mm
 1760 °F

@Thickness 0.126 in
 ISO 60695-2-12
Electrical Properties Metric English Comments
Surface Resistance 1.10e+14 ohm
1.10e+14 ohm
IEC 60093
Dielectric Constant 2.9
2.9
IEC 60250
Dielectric Strength 25.0 kV/mm
635 kV/in
IEC 60243
Comparative Tracking Index 600 V
600 V
Solution A; IEC 60112
Processing Properties Metric English Comments
Feed Temperature 230 - 235 °C
446 - 455 °F
Mold Temperature 60.0 - 80.0 °C
140 - 176 °F
Drying Temperature 80.0 °C
176 °F
Moisture Content <= 0.20 %
<= 0.20 %
Descriptive Properties Value Comments
Compression Zone 235-240°C
Mixing Zone 235-240°C