Solvay TECHNYLSTARâ„¢ S 218 V30 PA6, 30% glass filled, DRY

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled
Manufacturer Solvay
Trade Name TECHNYLSTAR™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay TECHNYLSTARâ„¢ S 218 V30 PA6, 30% glass filled, DRY.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: TECHNYLSTARâ„¢ S 218 V30 is based on a patented high flow polyamide 6 resin (TechnylStar), heat stabilized, reinforced with 30% of glass fiber, for injection molding. This product is available in black color.Benefits: Due to its outstanding flow characteristics, the product provides a significant productivity improvement and allows more freedom in mould and part design versus a standard polyamide solutions.Available in: Asia Pacific, Europe and North AmericaRegulations compliance: Grades produced or imported in Europe comply with directive 453/2010/EC, which amends REACH directive 1907/2006/EC. This grade complies with RoHS directive 2002/95/EC. Unless specified, this grade is not suitable for food contact, medical devices or toy applications.Applications: It is used in a wide variety of industries.Information provided by Rhodia, Rhodia has been acquired by Solvay.
Physical Properties Metric English Comments
Density 1.34 g/cc
0.0484 lb/in³
ISO 1183/A
Water Absorption 0.95 %

@Temperature 23.0 °C,
Time 86400 sec
0.95 %

@Temperature 73.4 °F,
Time 24.0 hour
ISO 62
Linear Mold Shrinkage 0.0054 cm/cm
0.0054 in/in
Isotropy
Linear Mold Shrinkage, Flow 0.0035 cm/cm
0.0035 in/in
Linear Mold Shrinkage, Transverse 0.0065 cm/cm
0.0065 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 190 MPa
27600 psi
ISO 527 Type 1A
Tensile Stress 85.0 MPa

@Strain 1.00 %
12300 psi

@Strain 1.00 %
145 MPa

@Strain 2.00 %
21000 psi

@Strain 2.00 %
170 MPa

@Strain 3.00 %
24700 psi

@Strain 3.00 %
Elongation at Break 3.8 %
3.8 %
ISO 527 Type 1A
Tensile Modulus 9.60 GPa
1390 ksi
ISO 527 Type 1A
Flexural Strength 255 MPa
37000 psi
ASTM D790
Flexural Modulus 8.40 GPa
1220 ksi
ISO 178
8.65 GPa
1250 ksi
ASTM D790
Izod Impact, Notched 1.00 J/cm
1.87 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 12.0 kJ/m²
5.71 ft-lb/in²
ISO 180/1eA
Izod Impact, Unnotched (ISO) 12.0 kJ/m²
5.71 ft-lb/in²
ISO 180/1eU
Charpy Impact Unnotched 8.10 J/cm²
38.5 ft-lb/in²
ISO 179/1eU
Charpy Impact, Notched 1.50 J/cm²
7.14 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 222 °C
432 °F
ISO 11357
Deflection Temperature at 1.8 MPa (264 psi) 205 °C
401 °F
ISO 75/Af
Flammability, UL94 HB

@Thickness 3.20 mm
HB

@Thickness 0.126 in
1210
Glow Wire Test 650 °C

@Thickness 1.60 mm
1200 °F

@Thickness 0.0630 in
ISO 60695-2-12
Electrical Properties Metric English Comments
Comparative Tracking Index 600 V
600 V
Solution A; IEC 60112
Processing Properties Metric English Comments
Feed Temperature 230 - 235 °C
446 - 455 °F
Mold Temperature 80.0 °C
176 °F
Drying Temperature 80.0 °C
176 °F
Moisture Content <= 0.20 %
<= 0.20 %
Descriptive Properties Value Comments
Compression Zone 235-240°C
Mixing Zone 240-245°C