Solvay TECHNYLSTARâ„¢ S 216 V30 PA6, 30% glass filled, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | Solvay |
| Trade Name | TECHNYLSTAR™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYLSTARâ„¢ S 216 V30 PA6, 30% glass filled, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: TECHNYL STAR TM Polyamide, reinforced with 30% of glass fiber, for injection molding. Characterized by a high fluidity of the melt.Available in: Asia Pacific, Europe and North AmericaProduct Applications: Due to its outstanding flow characteristics, TECHNYLSTAR TM S 216 V30 provides a significant productivity improvement and allows more freedom in mould design and part design versus standard polyamide solutions. This product is available in natural.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | ISO 1183/A |
| Water Absorption | 0.95 % @Temperature 23.0 °C, Time 86400 sec |
0.95 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 180 MPa | 26100 psi | ISO 527 Type 1A |
| Elongation at Break | 3.3 % | 3.3 % | ISO 527 Type 1A |
| Tensile Modulus | 9.60 GPa | 1390 ksi | ISO 527 Type 1A |
| Flexural Strength | 255 MPa | 37000 psi | ISO 178 |
| Flexural Modulus | 9.30 GPa | 1350 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | ISO 180/1eA |
| Izod Impact, Unnotched (ISO) | 82.0 kJ/m² | 39.0 ft-lb/in² | ISO 180/1eU |
| Charpy Impact Unnotched | 8.10 J/cm² | 38.5 ft-lb/in² | 23; ISO 179/1eU |
| 55.0 J/cm² | 262 ft-lb/in² | -30; ISO 179/1eU | |
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 32.0 µm/m-°C @Temperature 23.0 - 85.0 °C |
17.8 µin/in-°F @Temperature 73.4 - 185 °F |
ISO 11359 |
| Melting Point | 222 °C | 432 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 204 °C | 399 °F | ISO 75/Af |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
1210 |
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
1210 | |
| Oxygen Index | 22 % | 22 % | ISO 4589 |
| Glow Wire Test | 650 °C @Thickness 1.60 mm |
1200 °F @Thickness 0.0630 in |
ISO 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
| Dielectric Constant | 3.8 | 3.8 | IEC 60250 |
| Dissipation Factor | 0.020 | 0.020 | IEC 60250 |
| Comparative Tracking Index | 550 V | 550 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 220 - 225 °C | 428 - 437 °F | |
| Front Barrel Temperature | 235 - 245 °C | 455 - 473 °F | |
| Mold Temperature | 80.0 °C | 176 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 225-235°C |