Solvay TECHNYL® C 50 H2 PA6, DRY

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced
Manufacturer Solvay
Trade Name Technyl®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay TECHNYL® C 50 H2 PA6, DRY.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: TECHNYL® C 50H2 is a unreinforced melamine cyanurate flame retarded polyamide 6. This product is heat stabilized and can be used for injection molding and extrusion processes. This product is available in natural & black, and in other colors upon request.Benefits: This product, UL94 VO @ 0,4mm, offers excellent moldability together with good stiffness.Available in: Asia Pacific, Europe, Latin America and North AmericaRegulations compliance: Grades produced or imported in Europe comply with directive 453/2010/EC, which amends REACH directive 1907/2006/EC. This grade complies with RoHS directive 2002/95/EC. Unless specified, this grade is not suitable for food contact, medical devices or toy applications.Applications: Connectivity- junction blocks, terminal blocks, connectors…Information provided by Rhodia, Rhodia has been acquired by Solvay.
Physical Properties Metric English Comments
Density 1.16 g/cc
0.0419 lb/in³
ISO 1183/A
Water Absorption 1.1 %

@Temperature 23.0 °C,
Time 86400 sec
1.1 %

@Temperature 73.4 °F,
Time 24.0 hour
ISO 62
Linear Mold Shrinkage, Flow 0.013 cm/cm
0.013 in/in
Linear Mold Shrinkage, Transverse 0.0080 cm/cm
0.0080 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 60.0 MPa
8700 psi
ISO 527 Type 1A
80.0 MPa
11600 psi
ASTM D638
Tensile Strength, Yield 75.0 MPa
10900 psi
ISO 527 type 1 A
80.0 MPa
11600 psi
ASTM D638
Elongation at Break 15 %
15 %
ASTM D638
25 %
25 %
ISO 527 Type 1A
Elongation at Yield 3.5 %
3.5 %
ISO 527 type 1 A
Tensile Modulus 3.50 GPa
508 ksi
ISO 527 Type 1A
Flexural Strength 115 MPa
16700 psi
ASTM D790
200 MPa
29000 psi
ISO 178
Flexural Modulus 3.15 GPa
457 ksi
ISO 178
3.50 GPa
508 ksi
ASTM D790
Izod Impact, Notched 0.650 J/cm
1.22 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 3.50 kJ/m²
1.67 ft-lb/in²
ISO 180/1eA
Charpy Impact Unnotched 18.0 J/cm²
85.7 ft-lb/in²
ISO 179/1eU
Charpy Impact, Notched 0.600 J/cm²
2.86 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 222 °C
432 °F
ISO 11357
Deflection Temperature at 1.8 MPa (264 psi) 75.0 °C
167 °F
ISO 75/Af
Flammability, UL94 V-0

@Thickness 0.380 mm
V-0

@Thickness 0.0150 in
1210
V-0

@Thickness 0.800 mm
V-0

@Thickness 0.0315 in
1210
V-0

@Thickness 1.60 mm
V-0

@Thickness 0.0630 in
1210
V-0

@Thickness 3.20 mm
V-0

@Thickness 0.126 in
1210
Oxygen Index 36 %
36 %
ISO 4589
Glow Wire Test 700 °C

@Thickness 0.800 mm
1290 °F

@Thickness 0.0315 in
ignition temperature; ISO 60695-2-13
700 °C

@Thickness 1.60 mm
1290 °F

@Thickness 0.0630 in
ignition temperature; ISO 60695-2-13
700 °C

@Thickness 3.20 mm
1290 °F

@Thickness 0.126 in
ignition temperature; ISO 60695-2-13
960 °C

@Thickness 0.800 mm
1760 °F

@Thickness 0.0315 in
ISO 60695-2-12
960 °C

@Thickness 1.60 mm
1760 °F

@Thickness 0.0630 in
ISO 60695-2-12
960 °C

@Thickness 3.20 mm
1760 °F

@Thickness 0.126 in
ISO 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 60093
Surface Resistance 1.00e+15 ohm
1.00e+15 ohm
IEC 60093
Dielectric Constant 3.5
3.5
IEC 60250
Dielectric Strength 34.0 kV/mm
864 kV/in
IEC 60243
Dissipation Factor 0.020
0.020
IEC 60250
Comparative Tracking Index 475 V
475 V
Solution B; IEC 60112
600 V
600 V
Solution A; IEC 60112
Processing Properties Metric English Comments
Feed Temperature 230 - 235 °C
446 - 455 °F
Mold Temperature 70.0 - 100 °C
158 - 212 °F
Drying Temperature 80.0 °C
176 °F
Moisture Content <= 0.20 %
<= 0.20 %
Descriptive Properties Value Comments
Compression Zone 235-245°C
Fire and smoke F index I2/F3
NF F 16 101
Mixing Zone 245-250°C