Solvay TECHNYL® C 218 V 30 PA6, 30% glass fiber, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® C 218 V 30 PA6, 30% glass fiber, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: TECHNYL® C 218 V30 is a polyamide 6, heat stabilized, reinforced with 30% of glass fiber, for injection molding. This product is available in black color.Benefits: The product offers an excellent combination between thermal and mechanical properties.Available in: Asia Pacific, Europe, Latin America and North AmericaRegulations compliance: Grades produced or imported in Europe comply with directive 453/2010/EC, which amends REACH directive 1907/2006/EC. This grade complies with RoHS directive 2002/95/EC. Unless specified, this grade is not suitable for food contact, medical devices or toy applications.Applications: It is used in a wide variety of industries.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | ISO 1183/A |
| Water Absorption | 1.05 % @Temperature 23.0 °C, Time 86400 sec |
1.05 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 |
| Viscosity | 30 cP @Shear Rate 10000 1/s, Temperature 240 °C |
30 cP @Shear Rate 10000 1/s, Temperature 464 °F |
|
| 30 cP @Shear Rate 10000 1/s, Temperature 250 °C |
30 cP @Shear Rate 10000 1/s, Temperature 482 °F |
||
| 30 cP @Shear Rate 10000 1/s, Temperature 260 °C |
30 cP @Shear Rate 10000 1/s, Temperature 500 °F |
||
| 150 cP @Shear Rate 1000 1/s, Temperature 260 °C |
150 cP @Shear Rate 1000 1/s, Temperature 500 °F |
||
| 190 cP @Shear Rate 1000 1/s, Temperature 250 °C |
190 cP @Shear Rate 1000 1/s, Temperature 482 °F |
||
| 200 cP @Shear Rate 1000 1/s, Temperature 240 °C |
200 cP @Shear Rate 1000 1/s, Temperature 464 °F |
||
| 300 cP @Shear Rate 100 1/s, Temperature 260 °C |
300 cP @Shear Rate 100 1/s, Temperature 500 °F |
||
| 400 cP @Shear Rate 100 1/s, Temperature 250 °C |
400 cP @Shear Rate 100 1/s, Temperature 482 °F |
||
| 500 cP @Shear Rate 100 1/s, Temperature 240 °C |
500 cP @Shear Rate 100 1/s, Temperature 464 °F |
||
| Linear Mold Shrinkage | 0.0043 cm/cm | 0.0043 in/in | Isotropy |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm | 0.0070 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 170 MPa | 24700 psi | ASTM D638 |
| 190 MPa | 27600 psi | ISO 527 Type 1A | |
| Tensile Stress | 60.0 MPa @Strain 0.500 % |
8700 psi @Strain 0.500 % |
|
| 100 MPa @Strain 1.00 % |
14500 psi @Strain 1.00 % |
||
| 160 MPa @Strain 2.00 % |
23200 psi @Strain 2.00 % |
||
| 180 MPa @Strain 3.00 % |
26100 psi @Strain 3.00 % |
||
| Elongation at Break | 3.2 % | 3.2 % | ISO 527 Type 1A |
| 3.5 % | 3.5 % | ASTM D638 | |
| Tensile Modulus | 9.60 GPa | 1390 ksi | ISO 527 Type 1A |
| Flexural Strength | 255 MPa | 37000 psi | ISO 178 |
| Flexural Modulus | 8.40 GPa | 1220 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 14.0 kJ/m² | 6.66 ft-lb/in² | ISO 180/1eA |
| 125 kJ/m² | 59.5 ft-lb/in² | ASTM D256 | |
| Charpy Impact Unnotched | 9.20 J/cm² | 43.8 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 1.50 J/cm² | 7.14 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 32.0 µm/m-°C @Temperature 23.0 - 85.0 °C |
17.8 µin/in-°F @Temperature 73.4 - 185 °F |
ISO 11359 |
| Melting Point | 222 °C | 432 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO 75/Af |
| Flammability, UL94 | HB @Thickness 0.400 - 3.20 mm |
HB @Thickness 0.0157 - 0.126 in |
1210 |
| Oxygen Index | 23 % | 23 % | ISO 4589 |
| Glow Wire Test | 650 °C @Thickness 1.60 - 3.20 mm |
1200 °F @Thickness 0.0630 - 0.126 in |
ISO 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 |
| Dielectric Constant | 3.8 | 3.8 | IEC 60250 |
| Dissipation Factor | 0.020 | 0.020 | IEC 60250 |
| Comparative Tracking Index | 475 V | 475 V | Solution B; IEC 60112 |
| 600 V | 600 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 230 - 235 °C | 446 - 455 °F | |
| Mold Temperature | 70.0 - 100 °C | 158 - 212 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 235-245°C | |
| Mixing Zone | 245-250°C |
Users viewing this material also viewed the following:
- Network Polymers Kepital® F20-25
- Premix Thermoplastics PRE-ELEC® PP 1386
- ExxonMobil Escorene® LX-0252 LMDPE Rotational Molding Grade (discontinued **)
- Hybrid Plastics CO6U50.02 Nanoreinforced® Cyclic Olefin Copolymer
- Suzhou Hipro Polymers Hiprolon® 11 PES Colorized Nylon powder
- ExxonMobil 32 Mobil EAL Envirosyn H Series
- A. Schulman POLYBATCH™ U-7000-HS Blowing Agent Concentrate Based In HIPS
- ELASTO UK Dryflex® 602400S SEBS Based Material, Filled Qualities, 40A Hardness, Black
- 3M IC 15WB+ Fire Barrier Sealant
- Hexcel® HexForce™ 341 Fiber Glass Fabric
Copyright © lookpolymers.com All Rights Reserved