Solvay TECHNYL® B 216 Natural D PA66/6, Conditioned

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer Solvay
Trade Name Technyl®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay TECHNYL® B 216 Natural D PA66/6, Conditioned.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Unreinforced copolyamide 66/6, medium viscosity, for injection molding.Available in: EuropeProduct Applications: TECHNYL B 216 offers an excellent combination between impact resistance, rigidity, thermal resistance and surface appearance. It is used in a wide variety of industries (electrical, automotive). This grade is particularly suitable for molding perfume bottles which require a good scratch resistance. This product is available in a wide range of colors.Information provided by Rhodia, Rhodia has been acquired by Solvay.
Physical Properties Metric English Comments
Density 1.14 g/cc
0.0412 lb/in³
ISO 1183/A
Mechanical Properties Metric English Comments
Tensile Strength at Break 60.0 MPa
8700 psi
ISO 527 Type 1A
Tensile Strength, Yield 50.0 MPa
7250 psi
ISO 527 type 1 A
Elongation at Break 100 %
100 %
ISO 527 Type 1A
Elongation at Yield 25 %
25 %
ISO 527 type 1 A
Tensile Modulus 1.10 GPa
160 ksi
ISO 527 Type 1A
Flexural Strength 50.0 MPa
7250 psi
ISO 178
Flexural Modulus 1.20 GPa
174 ksi
ISO 178
Izod Impact, Notched (ISO) 16.0 kJ/m²
7.61 ft-lb/in²
ISO 180/1eA
Charpy Impact Unnotched NB
NB
ISO 179/1eU
Charpy Impact, Notched 1.60 J/cm²
7.61 ft-lb/in²
ISO 179/1eA
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+12 ohm-cm
1.00e+12 ohm-cm
IEC 60093
Surface Resistance 1.00e+12 ohm
1.00e+12 ohm
IEC 60093
Dielectric Constant 3.2
3.2
IEC 60250
Dielectric Strength 24.0 kV/mm
610 kV/in
IEC 60243
Dissipation Factor 0.10
0.10
IEC 60250
Comparative Tracking Index 600 V
600 V
Solution A; IEC 60112
Processing Properties Metric English Comments
Moisture Content <= 0.20 %
<= 0.20 %