Solvay TECHNYL® A 50H1 PA66, DRY

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer Solvay
Trade Name Technyl®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay TECHNYL® A 50H1 PA66, DRY.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Flame retardant polyamide 66, unreinforced, heat stabilized, for injection molding.Available in: Asia Pacific, Europe, Latin America and North AmericaProduct Applications: This phosphorus and halogen free flame retardant grade, offers excellent filling qualities combined with good stiffness. It is particularly suitable for molding insulating parts for electrical components: Components for electrical connections: junction blocks, terminal blocks, and connectors. This product is available in natural. Other colors can be provided upon requestInformation provided by Rhodia, Rhodia has been acquired by Solvay.
Physical Properties Metric English Comments
Density 1.16 g/cc
0.0419 lb/in³
ISO 1183/A
Water Absorption 0.88 %

@Temperature 23.0 °C,
Time 86400 sec
0.88 %

@Temperature 73.4 °F,
Time 24.0 hour
ISO 62
Linear Mold Shrinkage, Flow 0.0095 cm/cm
0.0095 in/in
Linear Mold Shrinkage, Transverse 0.011 cm/cm
0.011 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 75.0 MPa
10900 psi
ISO 527 Type 1A
Tensile Strength, Yield 86.0 MPa
12500 psi
ISO 527 type 1 A
Elongation at Break 21 %
21 %
ISO 527 Type 1A
Elongation at Yield 4.22 %
4.22 %
ISO 527 type 1 A
Tensile Modulus 3.80 GPa
551 ksi
ISO 527 Type 1A
Flexural Strength 137 MPa
19900 psi
ISO 178
Flexural Modulus 3.70 GPa
537 ksi
ISO 178
Izod Impact, Notched (ISO) 3.00 kJ/m²
1.43 ft-lb/in²
ISO 180/1eA
Charpy Impact Unnotched 13.0 J/cm²
61.9 ft-lb/in²
ISO 179/1eU
Charpy Impact, Notched 0.320 J/cm²
1.52 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 263 °C
505 °F
ISO 11357
Deflection Temperature at 0.46 MPa (66 psi) 237 °C
459 °F
ISO 75/Bf
Deflection Temperature at 1.8 MPa (264 psi) 85.0 °C
185 °F
ISO 75/Af
Flammability, UL94 V-0

@Thickness 0.380 mm
V-0

@Thickness 0.0150 in
1210
V-0

@Thickness 0.800 mm
V-0

@Thickness 0.0315 in
1210
V-0

@Thickness 1.60 mm
V-0

@Thickness 0.0630 in
1210
V-0

@Thickness 3.20 mm
V-0

@Thickness 0.126 in
1210
Glow Wire Test 725 °C

@Thickness 1.60 mm
1340 °F

@Thickness 0.0630 in
ignition temperature; ISO 60695-2-13
960 °C

@Thickness 0.800 mm
1760 °F

@Thickness 0.0315 in
ISO 60695-2-12
960 °C

@Thickness 1.60 mm
1760 °F

@Thickness 0.0630 in
ISO 60695-2-12
960 °C

@Thickness 3.20 mm
1760 °F

@Thickness 0.126 in
ISO 60695-2-12
Electrical Properties Metric English Comments
Comparative Tracking Index 60 V
60 V
Solution A; IEC 60112
Processing Properties Metric English Comments
Feed Temperature 265 - 275 °C
509 - 527 °F
Front Barrel Temperature 270 - 280 °C
518 - 536 °F
Mold Temperature 60.0 - 80.0 °C
140 - 176 °F
Drying Temperature 80.0 °C
176 °F
Moisture Content <= 0.20 %
<= 0.20 %
Descriptive Properties Value Comments
Compression Zone 265-275°C