Solvay TECHNYL® A 230 PA66, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® A 230 PA66, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Unreinforced and modified polyamide 66, with improved impact resistance, for injection molding.Available in: Europe and North AmericaProduct Applications: TECHNYL® A 230 offers excellent combination between rigidity and impact resistance at ambient temperature. This property save special conditioning before use parts (water absorption). This grade is commonly used for supple parts, such as: fasteners cable ties. This product is available in natural, grey and black.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ISO 1183/A |
| Water Absorption | 1.1 % @Temperature 23.0 °C, Time 86400 sec |
1.1 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | Isotropy |
| Linear Mold Shrinkage, Flow | 0.019 cm/cm | 0.019 in/in | |
| Linear Mold Shrinkage, Transverse | 0.019 cm/cm | 0.019 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 50.0 MPa | 7250 psi | ISO 527 Type 1A |
| Tensile Strength, Yield | 70.0 MPa | 10200 psi | ISO 527 type 1 A |
| Elongation at Break | 30 % | 30 % | ISO 527 Type 1A |
| Elongation at Yield | 5.0 % | 5.0 % | ISO 527 type 1 A |
| Tensile Modulus | 2.55 GPa | 370 ksi | ISO 527 Type 1A |
| Flexural Strength | 95.0 MPa | 13800 psi | ISO 178 |
| Flexural Modulus | 2.25 GPa | 326 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | ISO 180/1eA |
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU |
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 70.0 µm/m-°C @Temperature 23.0 - 85.0 °C |
38.9 µin/in-°F @Temperature 73.4 - 185 °F |
ISO 11359 |
| Oxygen Index | 21 % | 21 % | ISO 4589 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | IEC 60093 |
| Dielectric Constant | 3.2 | 3.2 | IEC 60250 |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | IEC 60243 |
| Dissipation Factor | 0.020 | 0.020 | IEC 60250 |
| Comparative Tracking Index | 475 V | 475 V | Solution B; IEC 60112 |
| 500 V | 500 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Front Barrel Temperature | 275 - 280 °C | 527 - 536 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
Users viewing this material also viewed the following:
- Parker Chomerics CHO-SEAL 1291 Conductive Elastomer
- Lehmann & Voss LUVOCOM® 80-7919 Polyacetal-copolymer, with PTFE, easy flowing
- Samsung Cheil Industries Starex® PT-0180 ABS, Unreinforced Painting Grade
- Sharadaa Ceramics REFCAST HA PLUS High Alumina Castables
- Sax Polymers SAXLAC 310U Acrylonitrile Butadiene Styrene
- Westlake Plastics Pomalux® Acetal Copolymer
- A. Schulman POLYBATCH™ Ivory 90033/4 Concentrate Based In LDPE
- Chevron Phillips MarFlex® 2121 Polyethylene; LDPE
- Ametek Ultra 303L P/M Stainless Steel, Sintered from 6.65 g/cc Green Density
Copyright © lookpolymers.com All Rights Reserved