Solvay TECHNYL® A 218HP V50 PA66, 35% glass fiber, DRY

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled
Manufacturer Solvay
Trade Name Technyl®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay TECHNYL® A 218HP V50 PA66, 35% glass fiber, DRY.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: TECHNYL® A 218HP V50 is a polyamide 66, reinforced with 50% of glass fiber, heat stabilized, for injection molding. This product is available in black color.Benefits: The product offers an outstanding long term heat resistance and is suitable to work in environments characterized by a very high temperature.Available in: Asia Pacific, Europe and Latin AmericaRegulations compliance: Grades produced or imported in Europe comply with directive 453/2010/EC, which amends REACH directive 1907/2006/EC. This grade complies with RoHS directive 2002/95/EC. Unless specified, this grade is not suitable for food contact, medical devices or toy applications.Applications: It is used in a wide variety of industries, especially in automotive industry for air circuit parts such as intercoolers.Information provided by Rhodia, Rhodia has been acquired by Solvay.
Physical Properties Metric English Comments
Density 1.52 g/cc
0.0549 lb/in³
ISO 1183/A
Linear Mold Shrinkage 0.0060 cm/cm
0.0060 in/in
Isotropy
Linear Mold Shrinkage, Flow 0.0030 cm/cm
0.0030 in/in
Linear Mold Shrinkage, Transverse 0.0050 cm/cm
0.0050 in/in
0.0090 cm/cm
0.0090 in/in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 200 MPa
29000 psi
ISO 527 Type 1A
Tensile Stress 39.0 MPa

@Strain 1.00 %,
Temperature 200 °C
 5660 psi

@Strain 1.00 %,
Temperature 392 °F
45.0 MPa

@Strain 2.00 %,
Temperature 200 °C
 6530 psi

@Strain 2.00 %,
Temperature 392 °F
48.0 MPa

@Strain 3.00 %,
Temperature 200 °C
 6960 psi

@Strain 3.00 %,
Temperature 392 °F
50.0 MPa

@Strain 4.00 %,
Temperature 200 °C
 7250 psi

@Strain 4.00 %,
Temperature 392 °F
80.0 MPa

@Strain 0.500 %,
Temperature 23.0 °C
 11600 psi

@Strain 0.500 %,
Temperature 73.4 °F
150 MPa

@Strain 1.00 %,
Temperature 23.0 °C
 21800 psi

@Strain 1.00 %,
Temperature 73.4 °F
180 MPa

@Strain 1.50 %,
Temperature 23.0 °C
 26100 psi

@Strain 1.50 %,
Temperature 73.4 °F
Elongation at Break 2.0 %
2.0 %
ISO 527 Type 1A
Tensile Modulus 15.0 GPa
2180 ksi
ISO 527 Type 1A
Flexural Strength 280 MPa
40600 psi
ASTM D790
320 MPa
46400 psi
ISO 178
Flexural Modulus 13.5 GPa
1960 ksi
ISO 178
13.5 GPa
1960 ksi
ASTM D790
Izod Impact, Notched (ISO) 20.0 kJ/m²
9.52 ft-lb/in²
ISO 180/1eA
Izod Impact, Unnotched (ISO) 80.0 kJ/m²
38.1 ft-lb/in²
ISO 180/1eU
Charpy Impact Unnotched 8.50 J/cm²
40.4 ft-lb/in²
ISO 179/1eU
Charpy Impact, Notched 1.70 J/cm²
8.09 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 263 °C
505 °F
ISO 11357
Deflection Temperature at 0.46 MPa (66 psi) 260 °C
500 °F
ISO 75/Bf
Deflection Temperature at 1.8 MPa (264 psi) 253 °C
487 °F
ISO 75/Af
Flammability, UL94 HB

@Thickness 0.800 mm
 HB

@Thickness 0.0315 in
 1210
HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
 1210
HB

@Thickness 3.20 mm
 HB

@Thickness 0.126 in
 1210
Processing Properties Metric English Comments
Feed Temperature 265 - 275 °C
509 - 527 °F
Mold Temperature 80.0 - 110 °C
176 - 230 °F
Drying Temperature 80.0 °C
176 °F
Moisture Content <= 0.12 %
<= 0.12 %
Descriptive Properties Value Comments
Compression Zone 270-280°C
Mixing Zone 280-290°C