Solvay TECHNYL® A 218 V35 PA66, 35% glass fiber, DRY

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled
Manufacturer Solvay
Trade Name Technyl®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay TECHNYL® A 218 V35 PA66, 35% glass fiber, DRY.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: TECHNYL® A 218 V35 is a polyamide 66, reinforced with 35% of glass fiber, heat stabilized, for injection molding. This product is available in natural and black colors.Benefits: The product offers an excellent combination between thermal and mechanical properties.Available in: Asia Pacific, Europe, Latin America and North AmericaRegulations compliance: Grades produced or imported in Europe comply with directive 453/2010/EC, which amends REACH directive 1907/2006/EC. This grade complies with RoHS directive 2002/95/EC. Unless specified, this grade is not suitable for food contact, medical devices or toy applicationsApplications: It is used in a wide variety of industries.Information provided by Rhodia, Rhodia has been acquired by Solvay.
Physical Properties Metric English Comments
Density 1.41 g/cc
0.0509 lb/in³
ISO 1183/A
Water Absorption 0.75 %

@Temperature 23.0 °C,
Time 86400 sec
0.75 %

@Temperature 73.4 °F,
Time 24.0 hour
ISO 62
Viscosity 20 cP

@Shear Rate 1000 1/s,
Temperature 280 °C
20 cP

@Shear Rate 1000 1/s,
Temperature 536 °F
20 cP

@Shear Rate 1000 1/s,
Temperature 290 °C
20 cP

@Shear Rate 1000 1/s,
Temperature 554 °F
20 cP

@Shear Rate 1000 1/s,
Temperature 300 °C
20 cP

@Shear Rate 1000 1/s,
Temperature 572 °F
120 cP

@Shear Rate 10.0 1/s,
Temperature 300 °C
120 cP

@Shear Rate 10.0 1/s,
Temperature 572 °F
135 cP

@Shear Rate 100 1/s,
Temperature 300 °C
135 cP

@Shear Rate 100 1/s,
Temperature 572 °F
140 cP

@Shear Rate 100 1/s,
Temperature 290 °C
140 cP

@Shear Rate 100 1/s,
Temperature 554 °F
150 cP

@Shear Rate 100 1/s,
Temperature 280 °C
150 cP

@Shear Rate 100 1/s,
Temperature 536 °F
250 cP

@Shear Rate 10.0 1/s,
Temperature 290 °C
250 cP

@Shear Rate 10.0 1/s,
Temperature 554 °F
300 cP

@Shear Rate 10.0 1/s,
Temperature 280 °C
300 cP

@Shear Rate 10.0 1/s,
Temperature 536 °F
Linear Mold Shrinkage 0.0060 cm/cm
0.0060 in/in
Isotropy
Linear Mold Shrinkage, Flow 0.0045 cm/cm
0.0045 in/in
Linear Mold Shrinkage, Transverse 0.0075 cm/cm
0.0075 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 210 MPa
30500 psi
ISO 527 Type 1A
Tensile Stress 40.0 MPa

@Strain 1.00 %,
Temperature 150 °C
5800 psi

@Strain 1.00 %,
Temperature 302 °F
45.0 MPa

@Strain 1.00 %,
Temperature 120 °C
6530 psi

@Strain 1.00 %,
Temperature 248 °F
60.0 MPa

@Strain 1.00 %,
Temperature 80.0 °C
8700 psi

@Strain 1.00 %,
Temperature 176 °F
65.0 MPa

@Strain 2.00 %,
Temperature 150 °C
9430 psi

@Strain 2.00 %,
Temperature 302 °F
75.0 MPa

@Strain 1.00 %,
Temperature 60.0 °C
10900 psi

@Strain 1.00 %,
Temperature 140 °F
75.0 MPa

@Strain 2.00 %,
Temperature 120 °C
10900 psi

@Strain 2.00 %,
Temperature 248 °F
80.0 MPa

@Strain 3.00 %,
Temperature 150 °C
11600 psi

@Strain 3.00 %,
Temperature 302 °F
90.0 MPa

@Strain 3.00 %,
Temperature 120 °C
13100 psi

@Strain 3.00 %,
Temperature 248 °F
90.0 MPa

@Strain 4.00 %,
Temperature 150 °C
13100 psi

@Strain 4.00 %,
Temperature 302 °F
90.0 MPa

@Strain 5.00 %,
Temperature 150 °C
13100 psi

@Strain 5.00 %,
Temperature 302 °F
95.0 MPa

@Strain 2.00 %,
Temperature 80.0 °C
13800 psi

@Strain 2.00 %,
Temperature 176 °F
95.0 MPa

@Strain 7.00 %,
Temperature 150 °C
13800 psi

@Strain 7.00 %,
Temperature 302 °F
100 MPa

@Strain 1.00 %,
Temperature 23.0 °C
14500 psi

@Strain 1.00 %,
Temperature 73.4 °F
100 MPa

@Strain 4.00 %,
Temperature 120 °C
14500 psi

@Strain 4.00 %,
Temperature 248 °F
105 MPa

@Strain 1.00 %,
Temperature -40.0 °C
15200 psi

@Strain 1.00 %,
Temperature -40.0 °F
105 MPa

@Strain 1.00 %,
Temperature 0.000 °C
15200 psi

@Strain 1.00 %,
Temperature 32.0 °F
105 MPa

@Strain 5.00 %,
Temperature 120 °C
15200 psi

@Strain 5.00 %,
Temperature 248 °F
105 MPa

@Strain 7.00 %,
Temperature 120 °C
15200 psi

@Strain 7.00 %,
Temperature 248 °F
110 MPa

@Strain 3.00 %,
Temperature 80.0 °C
16000 psi

@Strain 3.00 %,
Temperature 176 °F
122 MPa

@Strain 2.00 %,
Temperature 60.0 °C
17700 psi

@Strain 2.00 %,
Temperature 140 °F
125 MPa

@Strain 4.00 %,
Temperature 80.0 °C
18100 psi

@Strain 4.00 %,
Temperature 176 °F
125 MPa

@Strain 5.00 %,
Temperature 80.0 °C
18100 psi

@Strain 5.00 %,
Temperature 176 °F
140 MPa

@Strain 3.00 %,
Temperature 60.0 °C
20300 psi

@Strain 3.00 %,
Temperature 140 °F
150 MPa

@Strain 4.00 %,
Temperature 60.0 °C
21800 psi

@Strain 4.00 %,
Temperature 140 °F
150 MPa

@Strain 5.00 %,
Temperature 60.0 °C
21800 psi

@Strain 5.00 %,
Temperature 140 °F
155 MPa

@Strain 2.00 %,
Temperature 23.0 °C
22500 psi

@Strain 2.00 %,
Temperature 73.4 °F
190 MPa

@Strain 3.00 %,
Temperature 23.0 °C
27600 psi

@Strain 3.00 %,
Temperature 73.4 °F
200 MPa

@Strain 2.00 %,
Temperature 0.000 °C
29000 psi

@Strain 2.00 %,
Temperature 32.0 °F
210 MPa

@Strain 2.00 %,
Temperature -40.0 °C
30500 psi

@Strain 2.00 %,
Temperature -40.0 °F
Elongation at Break 3.0 %
3.0 %
ISO 527 Type 1A
Tensile Modulus 11.4 GPa
1650 ksi
ISO 527 Type 1A
Flexural Strength 290 MPa
42100 psi
ASTM D790
Flexural Modulus 9.50 GPa
1380 ksi
ISO 178
9.80 GPa
1420 ksi
ASTM D790
Izod Impact, Notched (ISO) 13.0 kJ/m²
6.19 ft-lb/in²
ISO 180/1eA
Charpy Impact Unnotched 9.50 J/cm²
45.2 ft-lb/in²
ISO 179/1eU
Charpy Impact, Notched 1.35 J/cm²
6.42 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 22.0 µm/m-°C

@Temperature 23.0 - 85.0 °C
12.2 µin/in-°F

@Temperature 73.4 - 185 °F
ISO 11359
Melting Point 263 °C
505 °F
ISO 11357
Deflection Temperature at 1.8 MPa (264 psi) 255 °C
491 °F
ISO 75/Af
Flammability, UL94 HB

@Thickness 0.800 mm
HB

@Thickness 0.0315 in
1210
HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
1210
HB

@Thickness 3.20 mm
HB

@Thickness 0.126 in
1210
Oxygen Index 23 %
23 %
ISO 4589
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 60093
Surface Resistance 6.00e+14 ohm
6.00e+14 ohm
IEC 60093
Dielectric Constant 3.7
3.7
IEC 60250
Dielectric Strength 34.0 kV/mm
864 kV/in
IEC 60243
Dissipation Factor 0.010
0.010
IEC 60250
Comparative Tracking Index 600 V
600 V
Solution A; IEC 60112
Processing Properties Metric English Comments
Feed Temperature 265 - 275 °C
509 - 527 °F
Mold Temperature 70.0 - 100 °C
158 - 212 °F
Drying Temperature 80.0 °C
176 °F