Solvay TECHNYL® A 218 V30 BK 34 NG PA66, 30% glass fiber, DRY

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled
Manufacturer Solvay
Trade Name Technyl®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay TECHNYL® A 218 V30 BK 34 NG PA66, 30% glass fiber, DRY.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: TECHNYL® A 218 V30 Black 34 NG is a polyamide 66, reinforced with 30% of glass fiber, heat stabilized, for injection molding. The product is available in black color.Benefits: This product has been specially designed to improve its resistance to automotive cooling liquids, increasing lifetime of parts in permanent contact with such a liquids.Available in: Asia Pacific, Europe, Latin America and North AmericaRegulations compliance: Grades produced or imported in Europe comply with directive 453/2010/EC, which amends REACH directive 1907/2006/EC. This grade complies with RoHS directive 2002/95/EC. Unless specified, this grade is not suitable for food contact, medical devices or toy applications.Applications: Cooling and heating radiator systems, header tanks, thermostat components, inlet & outlet pipes...Information provided by Rhodia, Rhodia has been acquired by Solvay.
Physical Properties Metric English Comments
Density 1.37 g/cc
0.0495 lb/in³
ISO 1183/A
Water Absorption 0.80 %

@Temperature 23.0 °C,
Time 86400 sec
 0.80 %

@Temperature 73.4 °F,
Time 24.0 hour
 ISO 62
Viscosity 20 cP

@Shear Rate 1000 1/s,
Temperature 280 °C
 20 cP

@Shear Rate 1000 1/s,
Temperature 536 °F
20 cP

@Shear Rate 1000 1/s,
Temperature 290 °C
 20 cP

@Shear Rate 1000 1/s,
Temperature 554 °F
20 cP

@Shear Rate 1000 1/s,
Temperature 300 °C
 20 cP

@Shear Rate 1000 1/s,
Temperature 572 °F
120 cP

@Shear Rate 10.0 1/s,
Temperature 300 °C
 120 cP

@Shear Rate 10.0 1/s,
Temperature 572 °F
135 cP

@Shear Rate 100 1/s,
Temperature 300 °C
 135 cP

@Shear Rate 100 1/s,
Temperature 572 °F
140 cP

@Shear Rate 100 1/s,
Temperature 290 °C
 140 cP

@Shear Rate 100 1/s,
Temperature 554 °F
150 cP

@Shear Rate 100 1/s,
Temperature 280 °C
 150 cP

@Shear Rate 100 1/s,
Temperature 536 °F
250 cP

@Shear Rate 10.0 1/s,
Temperature 290 °C
 250 cP

@Shear Rate 10.0 1/s,
Temperature 554 °F
300 cP

@Shear Rate 10.0 1/s,
Temperature 280 °C
 300 cP

@Shear Rate 10.0 1/s,
Temperature 536 °F
Linear Mold Shrinkage 0.0062 cm/cm
0.0062 in/in
Isotropy
Linear Mold Shrinkage, Flow 0.0050 cm/cm
0.0050 in/in
Linear Mold Shrinkage, Transverse 0.0080 cm/cm
0.0080 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 190 MPa
27600 psi
ISO 527 Type 1A
Tensile Stress 30.0 MPa

@Strain 1.00 %,
Temperature 120 °C
 4350 psi

@Strain 1.00 %,
Temperature 248 °F
40.0 MPa

@Strain 1.00 %,
Temperature 80.0 °C
 5800 psi

@Strain 1.00 %,
Temperature 176 °F
80.0 MPa

@Strain 1.00 %,
Temperature -30.0 °C
 11600 psi

@Strain 1.00 %,
Temperature -22.0 °F
80.0 MPa

@Strain 1.00 %,
Temperature 0.000 °C
 11600 psi

@Strain 1.00 %,
Temperature 32.0 °F
80.0 MPa

@Strain 1.00 %,
Temperature 23.0 °C
 11600 psi

@Strain 1.00 %,
Temperature 73.4 °F
80.0 MPa

@Strain 3.00 %,
Temperature 120 °C
 11600 psi

@Strain 3.00 %,
Temperature 248 °F
100 MPa

@Strain 3.00 %,
Temperature 80.0 °C
 14500 psi

@Strain 3.00 %,
Temperature 176 °F
100 MPa

@Strain 6.00 %,
Temperature 120 °C
 14500 psi

@Strain 6.00 %,
Temperature 248 °F
120 MPa

@Strain 6.00 %,
Temperature 80.0 °C
 17400 psi

@Strain 6.00 %,
Temperature 176 °F
165 MPa

@Strain 2.00 %,
Temperature 0.000 °C
 23900 psi

@Strain 2.00 %,
Temperature 32.0 °F
165 MPa

@Strain 2.00 %,
Temperature 23.0 °C
 23900 psi

@Strain 2.00 %,
Temperature 73.4 °F
178 MPa

@Strain 2.00 %,
Temperature -30.0 °C
 25800 psi

@Strain 2.00 %,
Temperature -22.0 °F
190 MPa

@Strain 3.00 %,
Temperature 23.0 °C
 27600 psi

@Strain 3.00 %,
Temperature 73.4 °F
195 MPa

@Strain 3.00 %,
Temperature 0.000 °C
 28300 psi

@Strain 3.00 %,
Temperature 32.0 °F
215 MPa

@Strain 3.00 %,
Temperature -30.0 °C
 31200 psi

@Strain 3.00 %,
Temperature -22.0 °F
Elongation at Break 3.0 %
3.0 %
ISO 527 Type 1A
Tensile Modulus 10.0 GPa
1450 ksi
ISO 527 Type 1A
Flexural Strength 280 MPa
40600 psi
ISO 178
290 MPa
42100 psi
ASTM D790
Flexural Modulus 9.00 GPa
1310 ksi
ISO 178
9.00 GPa
1310 ksi
ASTM D790
Izod Impact, Notched 1.15 J/cm
2.15 ft-lb/in
ASTM D256
Izod Impact, Unnotched (ISO) 10.0 kJ/m²
4.76 ft-lb/in²
ISO 180/1eU
Charpy Impact Unnotched 8.00 J/cm²
38.1 ft-lb/in²
ISO 179/1eU
4.20 J/cm²

@Temperature 135 °C,
Time 720000 sec
 20.0 ft-lb/in²

@Temperature 275 °F,
Time 200 hour
 ISO 179/1eU
7.00 J/cm²

@Temperature 120 °C,
Time 720000 sec
 33.3 ft-lb/in²

@Temperature 248 °F,
Time 200 hour
 ISO 179/1eU
Charpy Impact, Notched 1.10 J/cm²
5.23 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 25.0 µm/m-°C

@Temperature 23.0 - 85.0 °C
 13.9 µin/in-°F

@Temperature 73.4 - 185 °F
 ISO 11359
CTE, linear, Transverse to Flow 2.50 µm/m-°C

@Temperature 23.0 - 85.0 °C
 1.39 µin/in-°F

@Temperature 73.4 - 185 °F
 ISO 11359
Melting Point 263 °C
505 °F
ISO 11357
Deflection Temperature at 1.8 MPa (264 psi) 250 °C
482 °F
ISO 75/Af
255 °C
491 °F
ASTM D648
Flammability, UL94 HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
 1210
Oxygen Index 23 %
23 %
ISO 4589
Glow Wire Test 650 °C

@Thickness 1.60 mm
 1200 °F

@Thickness 0.0630 in
 ISO 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 60093
Surface Resistance 6.00e+14 ohm
6.00e+14 ohm
IEC 60093
Dielectric Constant 3.7
3.7
IEC 60250
Dielectric Strength 34.0 kV/mm
864 kV/in
IEC 60243
Dissipation Factor 0.010
0.010
IEC 60250
Comparative Tracking Index 500 V
500 V
Solution B; IEC 60112
600 V
600 V
Solution A; IEC 60112
Processing Properties Metric English Comments
Feed Temperature 265 - 275 °C
509 - 527 °F
Mold Temperature 70.0 - 100 °C
158 - 212 °F
Drying Temperature 80.0 °C
176 °F
Moisture Content <= 0.20 %
<= 0.20 %
Descriptive Properties Value Comments
Compression Zone 270-280°C
Mixing Zone 280-290°C