Solvay TECHNYL® A 218 V25 Black 21 N PA66, 25% glass fiber, DRY

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled
Manufacturer Solvay
Trade Name Technyl®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay TECHNYL® A 218 V25 Black 21 N PA66, 25% glass fiber, DRY.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: TECHNYL® A 218 V25 is a polyamide 66, reinforced with 25% of glass fiber, heat stabilized, for injection molding. This product is available in natural and black colors.Benefits: The product offers an excellent combination between thermal and mechanical properties.Available in: Asia Pacific, Europe and North America.Regulations compliance: Grades produced or imported in Europe comply with directive 453/2010/EC, which amends REACH directive 1907/2006/EC. This grade complies with RoHS directive 2002/95/EC. Unless specified, this grade is not suitable for food contact, medical devices or toy applications Applications: It is used in a wide variety of industries.Information provided by Rhodia, Rhodia has been acquired by Solvay.
Physical Properties Metric English Comments
Density 1.32 g/cc
0.0477 lb/in³
ISO 1183/A
Water Absorption 0.90 %

@Temperature 23.0 °C,
Time 86400 sec
 0.90 %

@Temperature 73.4 °F,
Time 24.0 hour
 ISO 62
Viscosity 30 cP

@Shear Rate 1000 1/s,
Temperature 280 °C
 30 cP

@Shear Rate 1000 1/s,
Temperature 536 °F
30 cP

@Shear Rate 1000 1/s,
Temperature 290 °C
 30 cP

@Shear Rate 1000 1/s,
Temperature 554 °F
30 cP

@Shear Rate 1000 1/s,
Temperature 300 °C
 30 cP

@Shear Rate 1000 1/s,
Temperature 572 °F
120 cP

@Shear Rate 100 1/s,
Temperature 280 °C
 120 cP

@Shear Rate 100 1/s,
Temperature 536 °F
120 cP

@Shear Rate 100 1/s,
Temperature 290 °C
 120 cP

@Shear Rate 100 1/s,
Temperature 554 °F
120 cP

@Shear Rate 100 1/s,
Temperature 300 °C
 120 cP

@Shear Rate 100 1/s,
Temperature 572 °F
200 cP

@Shear Rate 10.0 1/s,
Temperature 300 °C
 200 cP

@Shear Rate 10.0 1/s,
Temperature 572 °F
220 cP

@Shear Rate 10.0 1/s,
Temperature 290 °C
 220 cP

@Shear Rate 10.0 1/s,
Temperature 554 °F
290 cP

@Shear Rate 10.0 1/s,
Temperature 280 °C
 290 cP

@Shear Rate 10.0 1/s,
Temperature 536 °F
Linear Mold Shrinkage 0.0070 cm/cm
0.0070 in/in
Isotropy
Linear Mold Shrinkage, Flow 0.0060 cm/cm
0.0060 in/in
Linear Mold Shrinkage, Transverse 0.0085 cm/cm
0.0085 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 165 MPa
23900 psi
ISO 527 Type 1A
Tensile Stress 50.0 MPa

@Strain 2.50 %,
Temperature 120 °C
 7250 psi

@Strain 2.50 %,
Temperature 248 °F
59.0 MPa

@Strain 2.50 %,
Temperature 100 °C
 8560 psi

@Strain 2.50 %,
Temperature 212 °F
70.0 MPa

@Strain 5.00 %,
Temperature 120 °C
 10200 psi

@Strain 5.00 %,
Temperature 248 °F
79.0 MPa

@Strain 5.00 %,
Temperature 100 °C
 11500 psi

@Strain 5.00 %,
Temperature 212 °F
79.0 MPa

@Strain 10.0 %,
Temperature 120 °C
 11500 psi

@Strain 10.0 %,
Temperature 248 °F
81.0 MPa

@Strain 10.0 %,
Temperature 100 °C
 11700 psi

@Strain 10.0 %,
Temperature 212 °F
85.0 MPa

@Strain 2.50 %,
Temperature 60.0 °C
 12300 psi

@Strain 2.50 %,
Temperature 140 °F
105 MPa

@Strain 5.00 %,
Temperature 60.0 °C
 15200 psi

@Strain 5.00 %,
Temperature 140 °F
140 MPa

@Strain 2.50 %,
Temperature 23.0 °C
 20300 psi

@Strain 2.50 %,
Temperature 73.4 °F
Elongation at Break 3.0 %
3.0 %
ISO 527 Type 1A
4.0 %
4.0 %
ASTM D638
Tensile Modulus 8.40 GPa
1220 ksi
ISO 527 Type 1A
Flexural Strength 250 MPa
36300 psi
ASTM D790
Flexural Modulus 7.30 GPa
1060 ksi
ISO 178
7.30 GPa
1060 ksi
ASTM D790
Izod Impact, Notched (ISO) 8.50 kJ/m²
4.04 ft-lb/in²
ISO 180/1A
Charpy Impact Unnotched 5.70 J/cm²
27.1 ft-lb/in²
ISO 179/1eU
Charpy Impact, Notched 1.00 J/cm²
4.76 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 27.0 µm/m-°C

@Temperature 23.0 - 85.0 °C
 15.0 µin/in-°F

@Temperature 73.4 - 185 °F
 ISO 11359
CTE, linear, Transverse to Flow 2.70 µm/m-°C

@Temperature 23.0 - 85.0 °C
 1.50 µin/in-°F

@Temperature 73.4 - 185 °F
 ISO 11359
Melting Point 263 °C
505 °F
ISO 11357
Deflection Temperature at 1.8 MPa (264 psi) 245 °C
473 °F
ASTM D648
255 °C
491 °F
ISO 75/Af
Flammability, UL94 HB

@Thickness 0.380 mm
 HB

@Thickness 0.0150 in
 1210
HB

@Thickness 0.800 mm
 HB

@Thickness 0.0315 in
 1210
HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
 1210
HB

@Thickness 3.20 mm
 HB

@Thickness 0.126 in
 1210
Oxygen Index 23 %
23 %
ISO 4589
Glow Wire Test 650 °C

@Thickness 1.60 mm
 1200 °F

@Thickness 0.0630 in
 ISO 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 60093
Surface Resistance 6.00e+14 ohm
6.00e+14 ohm
IEC 60093
Dielectric Constant 3.7
3.7
IEC 60250
Dielectric Strength 32.0 kV/mm
813 kV/in
IEC 60243
Dissipation Factor 0.010
0.010
IEC 60250
Comparative Tracking Index 600 V
600 V
Solution A; IEC 60112
Processing Properties Metric English Comments
Feed Temperature 265 - 275 °C
509 - 527 °F
Mold Temperature 70.0 - 100 °C
158 - 212 °F
Drying Temperature 80.0 °C
176 °F
Moisture Content <= 0.20 %
<= 0.20 %
Descriptive Properties Value Comments
Compression Zone 270-280°C
Mixing Zone 280-290°C