Solvay TECHNYL® A 218 S40 Black 21 N PA66, 40% glass spheres, DRY

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Bead Filled
Manufacturer Solvay
Trade Name Technyl®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay TECHNYL® A 218 S40 Black 21 N PA66, 40% glass spheres, DRY.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Polyamide 66, reinforced with 40% of glass spheres, heat stabilized, for injection molding.Available in: EuropeProduct Applications: TECHNYL ® A 218 S40 is used in all sectors of industry, offering an excellent combination between thermal and mechanical properties. This grade is recommended for mechanical components which require a very good surface finish with low warpage, and good compression strength (bearing housings). This product is available in black.Information provided by Rhodia, Rhodia has been acquired by Solvay.
Physical Properties Metric English Comments
Density 1.47 g/cc
0.0531 lb/in³
ISO 1183/A
Water Absorption 0.70 %

@Temperature 23.0 °C,
Time 86400 sec
0.70 %

@Temperature 73.4 °F,
Time 24.0 hour
ISO 62
Linear Mold Shrinkage 0.010 cm/cm
0.010 in/in
Isotropy
Linear Mold Shrinkage, Flow 0.014 cm/cm
0.014 in/in
Linear Mold Shrinkage, Transverse 0.014 cm/cm
0.014 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 85.0 MPa
12300 psi
ISO 527 Type 1A
Tensile Strength, Yield 90.0 MPa
13100 psi
ISO 527 type 1 A
Elongation at Break 15 %
15 %
ISO 527 Type 1A
Elongation at Yield 4.0 %
4.0 %
ISO 527 type 1 A
Tensile Modulus 5.00 GPa
725 ksi
ISO 527 Type 1A
Flexural Strength 150 MPa
21800 psi
ISO 178
Flexural Modulus 4.70 GPa
682 ksi
ISO 178
Izod Impact, Notched (ISO) 3.00 kJ/m²
1.43 ft-lb/in²
ISO 180/1A
Charpy Impact Unnotched 2.50 J/cm²
11.9 ft-lb/in²
ISO 179/1eU
Charpy Impact, Notched 0.400 J/cm²
1.90 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 60.0 µm/m-°C

@Temperature 23.0 - 85.0 °C
33.3 µin/in-°F

@Temperature 73.4 - 185 °F
ISO 11359
Melting Point 263 °C
505 °F
ISO 11357
Deflection Temperature at 1.8 MPa (264 psi) 100 °C
212 °F
ISO 75/Af
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
1210
Oxygen Index 26 %
26 %
ISO 4589
Glow Wire Test 650 °C

@Thickness 1.60 mm
1200 °F

@Thickness 0.0630 in
ISO 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+14 ohm-cm
1.00e+14 ohm-cm
IEC 60093
Surface Resistance 5.00e+13 ohm
5.00e+13 ohm
IEC 60093
Dielectric Constant 4.0
4.0
IEC 60250
Dielectric Strength 30.0 kV/mm
762 kV/in
IEC 60243
Dissipation Factor 0.010
0.010
IEC 60250
Comparative Tracking Index 450 V
450 V
Solution A; IEC 60112
Processing Properties Metric English Comments
Feed Temperature 260 - 270 °C
500 - 518 °F
Front Barrel Temperature 280 - 290 °C
536 - 554 °F
Mold Temperature 60.0 - 80.0 °C
140 - 176 °F
Drying Temperature 80.0 °C
176 °F
Moisture Content <= 0.20 %
<= 0.20 %
Descriptive Properties Value Comments
Compression Zone 270-280°C