Solvay TECHNYL® A 216 NATURAL FA PA66, DRY

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer Solvay
Trade Name Technyl®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay TECHNYL® A 216 NATURAL FA PA66, DRY.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Unreinforced polyamide 66, medium viscosity, for injection molding.Available in: EuropeProduct Applications: TECHNYL® A 216 Natural FA offers all of the primary properties of unreinforced polyamide 66, such as: thermal and mechanical properties, impact resistance, abrasion and chemical resistance. This product is designed to be used in food contact applications specifically for cooking utensils. This product is available in natural and black colors.Information provided by Rhodia, Rhodia has been acquired by Solvay.
Physical Properties Metric English Comments
Density 1.14 g/cc
0.0412 lb/in³
ISO 1183/A
Water Absorption 1.3 %

@Temperature 23.0 °C,
Time 86400 sec
1.3 %

@Temperature 73.4 °F,
Time 24.0 hour
ISO 62
Linear Mold Shrinkage 0.010 cm/cm
0.010 in/in
Isotropy
Linear Mold Shrinkage, Flow 0.019 cm/cm
0.019 in/in
Linear Mold Shrinkage, Transverse 0.019 cm/cm
0.019 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 80.0 MPa
11600 psi
ISO 527 Type 1A
Tensile Strength, Yield 81.0 MPa
11700 psi
ISO 527 type 1 A
Elongation at Break 30 %
30 %
ISO 527 Type 1A
Elongation at Yield 4.2 %
4.2 %
ISO 527 type 1 A
Tensile Modulus 3.00 GPa
435 ksi
ISO 527 Type 1A
Flexural Strength 120 MPa
17400 psi
ISO 178
Flexural Modulus 2.90 GPa
421 ksi
ISO 178
Izod Impact, Notched (ISO) 4.00 kJ/m²
1.90 ft-lb/in²
ISO 180/1A
Charpy Impact Unnotched NB
NB
ISO 179/1eU
Charpy Impact, Notched 0.450 J/cm²
2.14 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 7.00 µm/m-°C

@Temperature 23.0 - 85.0 °C
3.89 µin/in-°F

@Temperature 73.4 - 185 °F
ISO 11359
CTE, linear, Transverse to Flow 2.50 µm/m-°C

@Temperature 23.0 - 85.0 °C
1.39 µin/in-°F

@Temperature 73.4 - 185 °F
ISO 11359
Melting Point 263 °C
505 °F
ISO 11357
Deflection Temperature at 1.8 MPa (264 psi) 75.0 °C
167 °F
ISO 75/Af
Flammability, UL94 V-2

@Thickness 0.800 mm
V-2

@Thickness 0.0315 in
ISO 1210
V-2

@Thickness 1.60 mm
V-2

@Thickness 0.0630 in
ISO 1210
Oxygen Index 26.5 %
26.5 %
ISO 4589
Glow Wire Test 650 °C

@Thickness 0.800 mm
1200 °F

@Thickness 0.0315 in
ISO 60695-2-12
650 °C

@Thickness 1.60 mm
1200 °F

@Thickness 0.0630 in
ISO 60695-2-12
650 °C

@Thickness 1.60 mm
1200 °F

@Thickness 0.0630 in
Ignition Temperature; ISO 60695-2-13
Electrical Properties Metric English Comments
Volume Resistivity 4.00e+14 ohm-cm
4.00e+14 ohm-cm
IEC 60093
Surface Resistance 1.00e+14 ohm
1.00e+14 ohm
IEC 60093
Dielectric Constant 2.9
2.9
IEC 60250
Dielectric Strength 30.0 kV/mm
762 kV/in
IEC 60243
Dissipation Factor 0.030
0.030
IEC 60250
Comparative Tracking Index 525 V
525 V
Solution B; IEC 60112
600 V
600 V
Solution A; IEC 60112
Processing Properties Metric English Comments
Feed Temperature 270 - 275 °C
518 - 527 °F
Front Barrel Temperature 285 - 290 °C
545 - 554 °F
Mold Temperature 60.0 - 80.0 °C
140 - 176 °F
Drying Temperature 80.0 °C
176 °F
Moisture Content <= 0.20 %
<= 0.20 %
Descriptive Properties Value Comments
Compression Zone 280-285°C