Solvay TECHNYL® A 208F PA66, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® A 208F PA66, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Unreinforced polyamide PA66, heat stabilized, high fluidity, fast cycling grade, for injection molding.Available in: EuropeProduct Applications: TECHNYL A 208F offers three main advantages: excellent filling qualities, good long term thermal properties and is V2 rated under 0.4 mm. according to UL94. It is particularly suitable for the molding of long parts with thin wall sections requiring good thermal resistance: cable ties and fasteners and connectors. This product is available in natural and black.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ISO 1183/A |
| Water Absorption | 1.2 % @Temperature 23.0 °C, Time 86400 sec |
1.2 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | Isotropy |
| Linear Mold Shrinkage, Flow | 0.020 cm/cm | 0.020 in/in | |
| Linear Mold Shrinkage, Transverse | 0.020 cm/cm | 0.020 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 60.0 MPa | 8700 psi | ISO 527 Type 1A |
| Tensile Strength, Yield | 85.0 MPa | 12300 psi | ISO 527 type 1 A |
| Elongation at Yield | 7.0 % | 7.0 % | ISO 527 type 1 A |
| Tensile Modulus | 3.20 GPa | 464 ksi | ISO 527 Type 1A |
| Flexural Modulus | 2.90 GPa | 421 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 4.50 kJ/m² | 2.14 ft-lb/in² | ISO 180/1A |
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU |
| Charpy Impact, Notched | 0.450 J/cm² | 2.14 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 12.6 µm/m-°C @Temperature 23.0 - 85.0 °C |
7.00 µin/in-°F @Temperature 73.4 - 185 °F |
ISO 11359 |
| Melting Point | 263 °C | 505 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | ISO 75/Af |
| Flammability, UL94 | V-2 @Thickness 0.380 mm |
V-2 @Thickness 0.0150 in |
ISO 1210 |
| V-2 @Thickness 0.800 mm |
V-2 @Thickness 0.0315 in |
ISO 1210 | |
| V-2 @Thickness 1.60 mm |
V-2 @Thickness 0.0630 in |
ISO 1210 | |
| Oxygen Index | 26 % | 26 % | ISO 4589 |
| Glow Wire Test | 650 °C @Thickness 1.60 mm |
1200 °F @Thickness 0.0630 in |
Ignition Temperature; ISO 60695-2-13 |
| 850 °C @Thickness 1.60 mm |
1560 °F @Thickness 0.0630 in |
ISO 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 |
| Dielectric Constant | 2.9 | 2.9 | IEC 60250 |
| Dielectric Strength | 27.0 kV/mm | 686 kV/in | IEC 60243 |
| Dissipation Factor | 0.030 | 0.030 | IEC 60250 |
| Comparative Tracking Index | 375 V | 375 V | Solution B; IEC 60112 |
| 475 V | 475 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 270 - 275 °C | 518 - 527 °F | |
| Front Barrel Temperature | 285 - 290 °C | 545 - 554 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Mixing Zone | 280-285°C |