Solvay TECHNYL® A 205F PA66, DRY

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer Solvay
Trade Name Technyl®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay TECHNYL® A 205F PA66, DRY.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: TECHNYL ® A 205F is an unreinforced polyamide 66 for injection molding. It is available in natural color.Benefits: The product offers two main advantages: excellent filling qualities and UL 94 V2 under 0.4 mm. It is particularly suitable for the molding of long parts with thin wall sections. Available in: Asia Pacific, Europe, Latin America and North AmericaRegulations compliance: Grades produced or imported in Europe comply with directive 453/2010/EC, which amends REACH directive 1907/2006/EC, This grade complies with RoHS directive 2002/95/EC. Unless specified, this grade is not suitable for food contact, medical devices or toy applications.Applications: Cable ties, fasteners or connectorsInformation provided by Rhodia, Rhodia has been acquired by Solvay.
Physical Properties Metric English Comments
Density 1.14 g/cc
0.0412 lb/in³
ISO 1183/A
Water Absorption 1.2 %

@Temperature 23.0 °C,
Time 86400 sec
 1.2 %

@Temperature 73.4 °F,
Time 24.0 hour
 ISO 62
Viscosity 20 cP

@Shear Rate 10000 1/s,
Temperature 300 °C
 20 cP

@Shear Rate 10000 1/s,
Temperature 572 °F
21 cP

@Shear Rate 10000 1/s,
Temperature 290 °C
 21 cP

@Shear Rate 10000 1/s,
Temperature 554 °F
22 cP

@Shear Rate 10000 1/s,
Temperature 280 °C
 22 cP

@Shear Rate 10000 1/s,
Temperature 536 °F
50 cP

@Shear Rate 1000 1/s,
Temperature 300 °C
 50 cP

@Shear Rate 1000 1/s,
Temperature 572 °F
80 cP

@Shear Rate 1000 1/s,
Temperature 290 °C
 80 cP

@Shear Rate 1000 1/s,
Temperature 554 °F
90 cP

@Shear Rate 100 1/s,
Temperature 300 °C
 90 cP

@Shear Rate 100 1/s,
Temperature 572 °F
101 cP

@Shear Rate 1000 1/s,
Temperature 280 °C
 101 cP

@Shear Rate 1000 1/s,
Temperature 536 °F
120 cP

@Shear Rate 100 1/s,
Temperature 280 °C
 120 cP

@Shear Rate 100 1/s,
Temperature 536 °F
120 cP

@Shear Rate 100 1/s,
Temperature 290 °C
 120 cP

@Shear Rate 100 1/s,
Temperature 554 °F
Linear Mold Shrinkage 0.010 cm/cm
0.010 in/in
Isotropy
Linear Mold Shrinkage, Flow 0.019 cm/cm
0.019 in/in
Linear Mold Shrinkage, Transverse 0.019 cm/cm
0.019 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 60.0 MPa
8700 psi
ISO 527 Type 1A
Tensile Stress 15.0 MPa

@Strain 10.0 %,
Temperature 150 °C
 2180 psi

@Strain 10.0 %,
Temperature 302 °F
19.0 MPa

@Strain 10.0 %,
Temperature 120 °C
 2760 psi

@Strain 10.0 %,
Temperature 248 °F
21.0 MPa

@Strain 20.0 %,
Temperature 150 °C
 3050 psi

@Strain 20.0 %,
Temperature 302 °F
24.0 MPa

@Strain 30.0 %,
Temperature 150 °C
 3480 psi

@Strain 30.0 %,
Temperature 302 °F
25.0 MPa

@Strain 10.0 %,
Temperature 80.0 °C
 3630 psi

@Strain 10.0 %,
Temperature 176 °F
25.0 MPa

@Strain 20.0 %,
Temperature 120 °C
 3630 psi

@Strain 20.0 %,
Temperature 248 °F
30.0 MPa

@Strain 30.0 %,
Temperature 120 °C
 4350 psi

@Strain 30.0 %,
Temperature 248 °F
39.0 MPa

@Strain 20.0 %,
Temperature 80.0 °C
 5660 psi

@Strain 20.0 %,
Temperature 176 °F
42.0 MPa

@Strain 30.0 %,
Temperature 80.0 °C
 6090 psi

@Strain 30.0 %,
Temperature 176 °F
45.0 MPa

@Strain 40.0 %,
Temperature 80.0 °C
 6530 psi

@Strain 40.0 %,
Temperature 176 °F
70.0 MPa

@Strain 2.50 %,
Temperature 23.0 °C
 10200 psi

@Strain 2.50 %,
Temperature 73.4 °F
Tensile Strength, Yield 85.0 MPa
12300 psi
ISO 527 type 1 A
155 MPa
22500 psi
ASTM D638
Elongation at Break 25 %
25 %
ASTM D638
50 %
50 %
ISO 527 Type 1A
Elongation at Yield 4.0 %
4.0 %
ISO 527 type 1 A
Tensile Modulus 3.20 GPa
464 ksi
ISO 527 Type 1A
Flexural Strength 120 MPa
17400 psi
ISO 178
125 MPa
18100 psi
ASTM D790
Flexural Modulus 3.00 GPa
435 ksi
ISO 178
3.35 GPa
486 ksi
ASTM D790
Izod Impact, Notched (ISO) 5.00 kJ/m²
2.38 ft-lb/in²
ISO 180/1A
80.0 kJ/m²
38.1 ft-lb/in²
ISO 180/1A
Charpy Impact Unnotched NB
NB
ISO 179/1eU
Charpy Impact, Notched 0.500 J/cm²
2.38 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 7.00 µm/m-°C

@Temperature 23.0 - 85.0 °C
 3.89 µin/in-°F

@Temperature 73.4 - 185 °F
 ISO 11359
CTE, linear, Transverse to Flow 7.00 µm/m-°C

@Temperature 23.0 - 85.0 °C
 3.89 µin/in-°F

@Temperature 73.4 - 185 °F
 ISO 11359
Melting Point 262 °C
504 °F
ASTM D3418
263 °C
505 °F
ISO 11357
Deflection Temperature at 1.8 MPa (264 psi) 80.0 °C
176 °F
ASTM D648
Flammability, UL94 V-2

@Thickness 0.400 mm
 V-2

@Thickness 0.0157 in
 ISO 1210
V-2

@Thickness 0.800 mm
 V-2

@Thickness 0.0315 in
 ISO 1210
V-2

@Thickness 1.60 mm
 V-2

@Thickness 0.0630 in
 ISO 1210
Oxygen Index 29 %
29 %
ISO 4589
Glow Wire Test 850 °C
1560 °F
ISO 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 60093
Surface Resistance 5.00e+14 ohm
5.00e+14 ohm
IEC 60093
Dielectric Constant 2.9
2.9
IEC 60250
Dielectric Strength 27.0 kV/mm
686 kV/in
IEC 60243
Dissipation Factor 0.030
0.030
IEC 60250
Comparative Tracking Index 550 V
550 V
Solution B; IEC 60112
600 V
600 V
Solution A; IEC 60112
Processing Properties Metric English Comments
Feed Temperature 265 - 275 °C
509 - 527 °F
Mold Temperature 60.0 - 80.0 °C
140 - 176 °F
Drying Temperature 80.0 °C
176 °F
Moisture Content <= 0.20 %
<= 0.20 %
Descriptive Properties Value Comments
Compression Zone 270-280°C