Solvay Specialty Polymers Veradel® 3320GF Polyethersulfone (PESU)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyethersulfone (PES) , Polyethersulfone (PES), 20%Glass Fiber Filled
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Veradel® 3320GF Polyethersulfone (PESU)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Veradel 3320GF is a 20% glass fiber reinforced grade of polyethersulfone (PESU). Adding glass fiber to polyethersulfone substantially increases the rigidity, tensile strength, creep resistance, dimensional stability and chemical resistance of the material, while maintaining most of its other basic characteristics. The combination of structural properties and cost effectiveness make this resin an attractive alternative to metals in many engineering applications. Veradel 3320GF is an opaque, grayish material in its natural form and can be readily colored. This grade was formerly marketed as Gafone™ PESU.Additional Information: 1. These properties has been determined from injection molded test specimen under ideal processing parameters and conditioned at 23+/- 2°C and 50%RH.Information provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Specific Gravity 1.49 g/cc
1.49 g/cc
ASTM D792
Filler Content 20 %
20 %
Glass Fiber Reinforcement
Water Absorption 0.50 %

@Time 86400 sec
0.50 %

@Time 24.0 hour
ASTM D570
Linear Mold Shrinkage, Flow 0.0030 cm/cm
0.0030 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength 120 MPa
17400 psi
ASTM D638
Elongation at Break 2.8 %
2.8 %
ASTM D638
Tensile Modulus 7.00 GPa
1020 ksi
ASTM D638
Flexural Strength 170 MPa
24700 psi
ASTM D790
Flexural Modulus 6.50 GPa
943 ksi
ASTM D790
Izod Impact, Notched 0.700 J/cm
1.31 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 25.0 µm/m-°C
13.9 µin/in-°F
ASTM D696
Maximum Service Temperature, Air 190 °C
374 °F
Continuous; ASTM D794
Deflection Temperature at 1.8 MPa (264 psi) 210 °C
410 °F
Annealed; ASTM D648
Flammability, UL94 V-0

@Thickness 0.800 mm
V-0

@Thickness 0.0315 in
UL 94
Oxygen Index 42 %
42 %
ASTM D2863
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
ASTM D257
Surface Resistance 1.00e+14 ohm
1.00e+14 ohm
ASTM D257
Dielectric Strength 20.0 kV/mm
508 kV/in
ASTM D149
Arc Resistance 110 sec
110 sec
ASTM D495
Comparative Tracking Index 150 V
150 V
UL 746
Processing Properties Metric English Comments
Die Temperature 300 - 320 °C
572 - 608 °F
Melt Temperature 340 - 380 °C
644 - 716 °F
Mold Temperature 120 - 160 °C
248 - 320 °F
Drying Temperature 150 °C
302 °F
Dry Time 3.00 hour
3.00 hour
Screw Speed 20 - 50 rpm
20 - 50 rpm
Descriptive Properties Value Comments
Appearance Colors Available
Opaque
Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
Features Acid Resistant
Flame Retardant
Good Adhesion
Good Creep Resistance
Good Dimensional Stability
High Rigidity
High Tensile Strength
Hydrolysis Resistant
Medium Flow
Medium Molecular Weight
Forms Pellets
Generic PESU
Processing Method Injection Molding
RoHS Compliance RoHS Compliant
Uses Metal Replacement